Preparation and Corrosion Resistance of Cerium and Silane Composite Passivation Film on Electrolytic Manganese Surface
摘 要
以硅烷偶联剂KH550和硝酸铈混合溶液为钝化液,通过浸泡法在电解锰表面成功制备了铈/硅烷复合钝化膜,并采用极化曲线、电化学阻抗谱、扫描电子显微图像(SEM)、衰减全反射傅里叶红外光谱(ATR-FTIR)及X射线光电子能谱(XPS)等对铈/硅烷复合钝化膜进行表征和分析。结果表明:电解锰腐蚀电位从钝化前的-1.364 V升高到钝化后的-1.225 V,腐蚀电流密度从3.58×10-5 A/cm2降低到1.91×10-6 A/cm2,极化电阻从461.18 Ω·cm2升高到4 706 Ω·cm2,电流阻碍效率达到了94.66%,所制备的钝化膜可显著提高电解锰的耐腐蚀性能。
Abstract
The cerium and silane composite passivation film on the surface of electrolytic manganese was successfully fabricated by immersing in passivation solution which was a mixture of silane coupling agent KH550 and cerium nitrate. The composite passivation film was characterized and analyzed through polarization curve, electrochemical impedance spectroscopy (EIS), scanning electron microscopy (SEM), attenuated total reflection Fourier transform infrared spectroscopy (ATR-FTIR) and X-ray photoelectron spectroscopy (XPS). It was found that the corrosion potential of electrolytic manganese increased from -1.364 V before passivation to -1.225 V after passivation, the corrosion current density decreased from 3.58×10-5 A/cm2 to 1.91×10-6 A/cm2, the polarization resistance increased from 461.18 Ω·cm2 to 4 706 Ω·cm2, and the current blocking efficiency reached 94.66%. The prepared passivation film could significantly improve the corrosion resistance of electrolytic manganese.
中图分类号 TG174.4 DOI 10.11973/fsyfh-202302005
所属栏目 试验研究
基金项目 国家自然科学基金地区科学基金项目(31560466);广西自然科学基金重点项目(2019GXNSFDA245025);广西科技重大专项(桂科AA18118013);广西高等学校高水平创新团队及卓越学者计划资助项目(桂教人[2014]7号)
收稿日期 2021/4/7
修改稿日期
网络出版日期
作者单位点击查看
引用该论文: CHEN Mengmeng,LI Shijia,LI Lijun,CHENG Hao. Preparation and Corrosion Resistance of Cerium and Silane Composite Passivation Film on Electrolytic Manganese Surface[J]. Corrosion & Protection, 2023, 44(2): 25
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】QIU P, LU F, WANG S, et al. Characterisation and anti-corrosion property of Ti conversion coating on manganese surface[J]. Corrosion Engineering, Science and Technology, 2020, 55(1):27-34.
【2】CAO Z F, LU F, QIU P, et al. Formation of a hydrophobic and corrosion resistant coating on manganese surface via stearic acid and oleic acid diethanolamide[J]. Colloids and Surfaces A:Physicochemical and Engineering Aspects, 2018, 555:372-380.
【3】CAO Z F, WANG J, QIU P, et al. Hydrophobic coatings for improving corrosion resistance of manganese substrate[J]. Surface and Coatings Technology, 2018, 347:235-244.
【4】郭晓斐, 王玥, 孙华, 等. 镀锌层三价铬钝化膜的制备工艺及性能研究[J]. 材料保护, 2012, 45(2):35-37, 48, 85.
【5】TIAN Z H, SHI H W, LIU F C, et al. Inhibiting effect of 8-hydroxyquinoline on the corrosion of silane-based Sol-gel coatings on AA 2024-T3[J]. Progress in Organic Coatings, 2015, 82:81-90.
【6】康佳, 刘胜林, 耿刚强, 等. 镀锌板无铬钝化技术研究进展[J]. 应用化工, 2017, 46(5):963-966, 971.
【7】姚知深, 牛宗伟, 刘斌, 等. 超声振动对65钢电解磷化膜表面形貌与耐蚀性的影响[J]. 电镀与精饰, 2019, 41(9):24-28.
【8】黄慧菊. Q235碳钢在含亚硝酸盐的酸性环境中腐蚀和钝化行为研究[D]. 武汉:武汉工程大学, 2019.
【9】王劲涛. 环氧改性水性硅酸盐富锌涂层防腐性能及机理[D]. 大连:大连海事大学, 2020.
【10】杨灿. 电解金属锰无铬钝化工艺研究[D]. 重庆:重庆大学, 2009.
【11】汪玉瑄, 王清国, 朱雅男, 等. 无毒环保型水基防锈剂的研制与应用[J]. 汽车工艺与材料, 2013(11):60-65.
【12】徐在培. 磷、硫元素对钢水成分的影响[J]. 一重技术, 2006(5):74, 73.
【13】LU F, CAO Z F, YANG F, et al. Fabrication of hydrophobic coating on electrolytic manganese surface for enhancing corrosion resistance[J]. Progress in Organic Coatings, 2019, 132:379-387.
【14】杨萍. 电解锰无硒、无铬清洁制备技术的研究及应用[D]. 长沙:中南大学, 2013.
【15】罗钊, 韩凤兰, 刘贵群, 等. 电解锰在NaCl溶液中的腐蚀行为[J]. 腐蚀与防护, 2016, 37(1):39-42, 46.
【16】杨超, 田熙科, 邓德义, 等. 用于电解金属锰表面处理的无铬钝化剂及其制备方法:CN101824615A[P]. 2010-09-08.
【17】邹兴, 邹恩阳, 张虹. 一种金属锰钝化液及其使用方法:CN1752286A[P]. 2006-03-29.
【18】彭纱, 陈虹玮, 孙琳, 等. 铝材表面杂化硅烷薄膜的制备及耐蚀性[J]. 铝加工, 2019(6):14-18.
【19】龚利华, 朱玉巧, 程东亮. 镀锌钢板表面有机硅烷钝化膜的耐蚀性研究[J]. 表面技术, 2011, 40(1):34-36, 85.
【20】DASTGHEIB A, ATTAR M M, ZAREBIDAKI A. Evaluation of corrosion inhibition of mild steel in 3.5 wt% NaCl solution by cerium nitrate[J]. Metals and Materials International, 2020, 26(11):1634-1642.
【21】BRACHETTI-SIBAJA S B, DOMÍNGUEZ-CRESPO M A, TORRES-HUERTA A M, et al. Fabrication of sputtered Ce/La, La/Ce oxide bilayers on AA6061 and AA7075 aluminum alloys for the development of corrosion protective coatings[J]. Materials, 2018, 11(7):1114.
【22】FORSYTH, WILSON, BEHRSING, et al. Effectiveness of rare-earth metal compounds as corrosion inhibitors for steel[J]. Corrosion, 2006, 58(11):953-960.
【23】杨宁, 龙晋明. 稀土钝化——金属防腐蚀表面处理新技术[J]. 稀土, 2002, 23(2):55-62.
【24】苗伟俊, 张余宝, 古宁宇, 等. 表面硅烷化铜箔的电化学腐蚀与防护研究[J]. 电化学, 2012, 18(4):359-364.
【25】谢荟, 何江, 何德良. 水基硅烷化溶液中铝表面硅烷-铈盐杂化膜的制备及表征[J]. 电镀与涂饰, 2015, 34(14):821-827.
【26】唐莎巍. 预处理对Al18B4O33w/6061复合材料表面稀土转化膜腐蚀行为的影响[D]. 哈尔滨:哈尔滨工业大学, 2007.
【27】朱霏. 硅烷基无铬钝化液制备及其耐蚀机理研究[D]. 昆明:昆明理工大学, 2019.
【28】李锋. 热浸镀锌钢板表面有机无机复合钝化工艺开发及其机理研究[D]. 西安:长安大学, 2019.
【29】崔珊. 铝及铝合金无铬钝化工艺及性能研究[D]. 沈阳:沈阳理工大学, 2017.
【30】张瑜, 赵佳新, 代永祺, 等. 硝酸铈对镁合金锌、锰系磷酸盐转化膜性能的影响[J]. 电镀与环保, 2019, 39(4):58-61.
【31】高晓辉. 镁锂合金表面硅烷复合耐蚀膜层的制备及性能研究[D]. 哈尔滨:哈尔滨工程大学, 2017.
【32】董金美, 李颖, 文静, 等. KH550硅烷偶联剂的水解工艺研究[J]. 盐湖研究, 2020, 28(3):28-33.
【33】王凡非, 冯启明, 王维清, 等. 硅烷偶联剂KH550对超细石英粉的改性[J]. 材料导报, 2014, 28(18):70-73, 98.
【34】单芙蓉, 于志明, 罗丽丝, 等. 硅烷偶联剂KH550表面改性纳米Al2O3的研究[J]. 化工新型材料, 2013, 41(5):169-170, 185.
【35】单凤君, 王双红, 刘常升, 等. 热镀锌钢板表面氨基硅烷膜的制备及其耐腐蚀性能[J]. 材料保护, 2011, 44(1):6-9, 6.
【36】BECHE E, CHARVIN P, PERARNAU D, et al. Ce 3d XPS investigation of cerium oxides and mixed cerium oxide (CexTiyOz)[J]. Surface and Interface Analysis, 2008, 40(3/4):264-267.
【37】YUE Y Y, LIU Z X, WAN T T, et al. Effect of phosphate-silane pretreatment on the corrosion resistance and adhesive-bonded performance of the AZ31 magnesium alloys[J]. Progress in Organic Coatings, 2013, 76(5):835-843.
【38】杨明, 陈国美, 倪自丰, 等. 40Cr基体表面GO/BTESPT硅烷复合膜的制备和性能表征[J]. 电镀与精饰, 2020, 42(9):16-23.
【2】CAO Z F, LU F, QIU P, et al. Formation of a hydrophobic and corrosion resistant coating on manganese surface via stearic acid and oleic acid diethanolamide[J]. Colloids and Surfaces A:Physicochemical and Engineering Aspects, 2018, 555:372-380.
【3】CAO Z F, WANG J, QIU P, et al. Hydrophobic coatings for improving corrosion resistance of manganese substrate[J]. Surface and Coatings Technology, 2018, 347:235-244.
【4】郭晓斐, 王玥, 孙华, 等. 镀锌层三价铬钝化膜的制备工艺及性能研究[J]. 材料保护, 2012, 45(2):35-37, 48, 85.
【5】TIAN Z H, SHI H W, LIU F C, et al. Inhibiting effect of 8-hydroxyquinoline on the corrosion of silane-based Sol-gel coatings on AA 2024-T3[J]. Progress in Organic Coatings, 2015, 82:81-90.
【6】康佳, 刘胜林, 耿刚强, 等. 镀锌板无铬钝化技术研究进展[J]. 应用化工, 2017, 46(5):963-966, 971.
【7】姚知深, 牛宗伟, 刘斌, 等. 超声振动对65钢电解磷化膜表面形貌与耐蚀性的影响[J]. 电镀与精饰, 2019, 41(9):24-28.
【8】黄慧菊. Q235碳钢在含亚硝酸盐的酸性环境中腐蚀和钝化行为研究[D]. 武汉:武汉工程大学, 2019.
【9】王劲涛. 环氧改性水性硅酸盐富锌涂层防腐性能及机理[D]. 大连:大连海事大学, 2020.
【10】杨灿. 电解金属锰无铬钝化工艺研究[D]. 重庆:重庆大学, 2009.
【11】汪玉瑄, 王清国, 朱雅男, 等. 无毒环保型水基防锈剂的研制与应用[J]. 汽车工艺与材料, 2013(11):60-65.
【12】徐在培. 磷、硫元素对钢水成分的影响[J]. 一重技术, 2006(5):74, 73.
【13】LU F, CAO Z F, YANG F, et al. Fabrication of hydrophobic coating on electrolytic manganese surface for enhancing corrosion resistance[J]. Progress in Organic Coatings, 2019, 132:379-387.
【14】杨萍. 电解锰无硒、无铬清洁制备技术的研究及应用[D]. 长沙:中南大学, 2013.
【15】罗钊, 韩凤兰, 刘贵群, 等. 电解锰在NaCl溶液中的腐蚀行为[J]. 腐蚀与防护, 2016, 37(1):39-42, 46.
【16】杨超, 田熙科, 邓德义, 等. 用于电解金属锰表面处理的无铬钝化剂及其制备方法:CN101824615A[P]. 2010-09-08.
【17】邹兴, 邹恩阳, 张虹. 一种金属锰钝化液及其使用方法:CN1752286A[P]. 2006-03-29.
【18】彭纱, 陈虹玮, 孙琳, 等. 铝材表面杂化硅烷薄膜的制备及耐蚀性[J]. 铝加工, 2019(6):14-18.
【19】龚利华, 朱玉巧, 程东亮. 镀锌钢板表面有机硅烷钝化膜的耐蚀性研究[J]. 表面技术, 2011, 40(1):34-36, 85.
【20】DASTGHEIB A, ATTAR M M, ZAREBIDAKI A. Evaluation of corrosion inhibition of mild steel in 3.5 wt% NaCl solution by cerium nitrate[J]. Metals and Materials International, 2020, 26(11):1634-1642.
【21】BRACHETTI-SIBAJA S B, DOMÍNGUEZ-CRESPO M A, TORRES-HUERTA A M, et al. Fabrication of sputtered Ce/La, La/Ce oxide bilayers on AA6061 and AA7075 aluminum alloys for the development of corrosion protective coatings[J]. Materials, 2018, 11(7):1114.
【22】FORSYTH, WILSON, BEHRSING, et al. Effectiveness of rare-earth metal compounds as corrosion inhibitors for steel[J]. Corrosion, 2006, 58(11):953-960.
【23】杨宁, 龙晋明. 稀土钝化——金属防腐蚀表面处理新技术[J]. 稀土, 2002, 23(2):55-62.
【24】苗伟俊, 张余宝, 古宁宇, 等. 表面硅烷化铜箔的电化学腐蚀与防护研究[J]. 电化学, 2012, 18(4):359-364.
【25】谢荟, 何江, 何德良. 水基硅烷化溶液中铝表面硅烷-铈盐杂化膜的制备及表征[J]. 电镀与涂饰, 2015, 34(14):821-827.
【26】唐莎巍. 预处理对Al18B4O33w/6061复合材料表面稀土转化膜腐蚀行为的影响[D]. 哈尔滨:哈尔滨工业大学, 2007.
【27】朱霏. 硅烷基无铬钝化液制备及其耐蚀机理研究[D]. 昆明:昆明理工大学, 2019.
【28】李锋. 热浸镀锌钢板表面有机无机复合钝化工艺开发及其机理研究[D]. 西安:长安大学, 2019.
【29】崔珊. 铝及铝合金无铬钝化工艺及性能研究[D]. 沈阳:沈阳理工大学, 2017.
【30】张瑜, 赵佳新, 代永祺, 等. 硝酸铈对镁合金锌、锰系磷酸盐转化膜性能的影响[J]. 电镀与环保, 2019, 39(4):58-61.
【31】高晓辉. 镁锂合金表面硅烷复合耐蚀膜层的制备及性能研究[D]. 哈尔滨:哈尔滨工程大学, 2017.
【32】董金美, 李颖, 文静, 等. KH550硅烷偶联剂的水解工艺研究[J]. 盐湖研究, 2020, 28(3):28-33.
【33】王凡非, 冯启明, 王维清, 等. 硅烷偶联剂KH550对超细石英粉的改性[J]. 材料导报, 2014, 28(18):70-73, 98.
【34】单芙蓉, 于志明, 罗丽丝, 等. 硅烷偶联剂KH550表面改性纳米Al2O3的研究[J]. 化工新型材料, 2013, 41(5):169-170, 185.
【35】单凤君, 王双红, 刘常升, 等. 热镀锌钢板表面氨基硅烷膜的制备及其耐腐蚀性能[J]. 材料保护, 2011, 44(1):6-9, 6.
【36】BECHE E, CHARVIN P, PERARNAU D, et al. Ce 3d XPS investigation of cerium oxides and mixed cerium oxide (CexTiyOz)[J]. Surface and Interface Analysis, 2008, 40(3/4):264-267.
【37】YUE Y Y, LIU Z X, WAN T T, et al. Effect of phosphate-silane pretreatment on the corrosion resistance and adhesive-bonded performance of the AZ31 magnesium alloys[J]. Progress in Organic Coatings, 2013, 76(5):835-843.
【38】杨明, 陈国美, 倪自丰, 等. 40Cr基体表面GO/BTESPT硅烷复合膜的制备和性能表征[J]. 电镀与精饰, 2020, 42(9):16-23.
相关信息