55SiCrA钢弹簧断裂原因
Fracture reason of 55SiCrA steel spring
摘 要
采用宏观观察、化学成分分析、显微硬度测试、金相检验、扫描电镜分析等方法分析了55SiCrA钢弹簧疲劳断裂的原因。结果表明:弹簧内、外侧表面缺陷为潜在的裂纹源,在疲劳测试过程中,缺陷处极易形成应力集中并产生裂纹,裂纹不断扩展,最终导致弹簧断裂。
表面缺陷
疲劳断裂
硬度测试
55SiCrA steel spring
surface defect
fatigue fracture
hardness test
Abstract
The causes of fatigue fracture of 55SiCrA steel spring were analyzed by means of macroscopic observation, chemical composition analysis, microhardness test, metallographic examination and scanning electron microscope analysis. The results show that the inner and outer surface defects of the spring were potential crack sources, which were easy to form stress concentration and produce cracks, and the cracks continued to expand, eventually led to spring fracture.
中图分类号 TB31 TG115.2 DOI 10.11973/lhjy-wl202304005
所属栏目 质量控制与失效分析
基金项目
收稿日期 2022/4/23
修改稿日期
网络出版日期
作者单位点击查看
备注侯兴辉(1984-),男,本科,高级工程师,主要从事钢铁材料的产品检测和质量管理工作
引用该论文: HOU Xinghui,WANG Xiaolan,JI Cannan,LU Xuxia. Fracture reason of 55SiCrA steel spring[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2023, 59(4): 15～18
侯兴辉,王晓兰,季灿南,陆旭霞. 55SiCrA钢弹簧断裂原因[J]. 理化检验－物理分册, 2023, 59(4): 15～18
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】张正贵,李平,李姗姗,等.60Si2MnA盘簧断裂失效分析[J].金属热处理,2014,39(12):156-158.
【2】肖洪秀,伍曾,黄新杰.高铁扣件弹条疲劳断裂原因分析[J].工业安全与环保,2021,47(2):50-54.
【3】聂轮.气门弹簧早期断裂原因[J].理化检验(物理分册),2021,57(4):55-57.
【4】叶圣渊,徐道送,徐旋旋,等.60Si2MnA钢弹簧断裂失效分析[J].物理测试,2018,36(5):44-47.
【2】肖洪秀,伍曾,黄新杰.高铁扣件弹条疲劳断裂原因分析[J].工业安全与环保,2021,47(2):50-54.
【3】聂轮.气门弹簧早期断裂原因[J].理化检验(物理分册),2021,57(4):55-57.
【4】叶圣渊,徐道送,徐旋旋,等.60Si2MnA钢弹簧断裂失效分析[J].物理测试,2018,36(5):44-47.
相关信息