Comparison of In-Situ Monitoring Methods for Soil Corrosion of Grounding Galvanized Round Steel
摘 要
分别采用失重法、护环电极法和电化学阻抗法研究了埋设在武汉土壤环境中接地镀锌圆钢的腐蚀行为,对比了各监测技术的相关性。结果表明:埋设1~2月时,试样的腐蚀速率较大,随后逐渐减小;试样表面镀锌层溶解不均匀,埋设3月后残留的镀锌层已很少;电化学阻抗法测量的极化电阻与腐蚀速率之间的相关性较好,但由于镀锌层与Q235钢基体所形成电偶的影响,不能按传统方法直接计算得到腐蚀速率;在合适条件下,现场采用护环电极法得到的极化电阻与电化学阻抗谱法得到的极化电阻具有可比性。
Abstract
The corrosion behavior of grounding galvanized round steel buried in soil environment of Wuhan was studied by weight loss method, guard ring electrode method and electrochemical impedance method, and the correlation of the monitoring techniques was compared. The results showed that the corrosion rate of the sample was large when buried for 1-2 months, and then gradually decreased. The dissolution of the zinc coating was uneven, and there was little residual zinc coating on the sample surface after 3 months of burial. The polarization resistance measured by electrochemical impedance method displayed a good correlation with corrosion rate. However, due to the influence of the galvanic couple between zinc coating and Q235 steel substrate, the corrosion rate cannot be directly calculated using traditional method. Under appropriate conditions, the polarization resistance obtained by guard ring electrode method could be comparable to that measured with electrochemical impedance method.
中图分类号 TG172 DOI 10.11973/fsyfh-202308003
所属栏目 腐蚀监检测技术及其应用
基金项目 国家电网有限公司总部管理科技项目(5500-202126130A-0-0-00)
收稿日期 2023/4/14
修改稿日期
网络出版日期
作者单位点击查看
联系人作者徐霞(254408546@qq.com)
引用该论文: XU Xia,LIU Fan,TANG Liangliang,FAN Songhai,LEI Xiao,LIU Gang,CHEN Huirong,WU Min. Comparison of In-Situ Monitoring Methods for Soil Corrosion of Grounding Galvanized Round Steel[J]. Corrosion & Protection, 2023, 44(8): 13
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】耿进锋, 时洪飞. 变电站接地网腐蚀与防护技术进展[J]. 腐蚀与防护, 2009, 30(8):523-525.
【2】魏巍, 吴欣强, 柯伟, 等. 接地网材料腐蚀与防护研究进展[J]. 腐蚀科学与防护技术, 2015, 27(3):273-277.
【3】朱忠伟, 吴一平, 葛红花. 变电站接地网腐蚀与防护研究进展[J]. 上海电力学院学报, 2009, 25(6):570-574.
【4】吕旺燕, 刘世念, 苏伟, 等. 变电站接地网腐蚀与防护技术的研究进展[J]. 全面腐蚀控制, 2013, 27(12):26-30.
【5】江培柯. 新型接地材料的腐蚀规律研究[D]. 宜昌:三峡大学, 2021.
【6】徐立. Q235钢、锌和镀锌钢在武汉土壤环境中的腐蚀行为研究[D]. 北京:机械科学研究总院, 2020.
【7】邓盼, 周艺, 朱志平, 等. 接地网材料在土壤中的腐蚀现状及腐蚀机理分析[J]. 广东化工, 2015, 42(4):12-14, 23.
【8】郭安祥, 胡尾娟, 闫爱军, 等. 不锈钢、镀锌钢接地材料在土壤中的腐蚀规律研究[J]. 材料导报, 2015, 29(S2):498-501.
【9】SCULLY J R. Polarization resistance method for determination of instantaneous corrosion rates[J]. Corrosion, 2000, 56(2):199-218.
【10】XIA D H, DENG C M, MACDONALD D, et al. Electrochemical measurements used for assessment of corrosion and protection of metallic materials in the field:a critical review[J]. Journal of Materials Science & Technology, 2022, 112:151-183.
【11】XIA D H, JI Y Y, ZHANG R F, et al. On the localized corrosion of AA5083 in a simulated dynamic seawater/air interface-part 1:corrosion initiation mechanism[J]. Corrosion Science, 2023, 213:110985.
【12】冯南战, 李志忠, 李亨特, 等. 高压变电站接地网的腐蚀防护与监测技术研究进展[J]. 腐蚀科学与防护技术, 2018, 30(3):331-338.
【13】LAW D W, MILLARD S G, BUNGEY J H. Effect of electrode orientation on linear polarisation measurements using sensor controlled guard ring[J]. British Corrosion Journal, 2000, 35(2):136-140.
【14】POURSAEE A, HANSSON C M. Galvanostatic pulse technique with the current confinement guard ring:the laboratory and finite element analysis[J]. Corrosion Science, 2008, 50(10):2739-2746.
【15】寄玉玉, 王佩, 张秀丽, 等. 接地网腐蚀状态原位检测技术研究[J]. 华北电力技术, 2012(8):34-37.
【16】王天正, 徐霞, 郝晋堂, 等. 高压变电站接地网的远程腐蚀监测技术[J]. 腐蚀科学与防护技术, 2016, 28(2):184-188.
【17】黄涛. 变电站接地网材料在模拟土壤中的腐蚀行为研究[D]. 昆明:昆明理工大学, 2014.
【18】曹楚南. 腐蚀电化学原理[M]. 3版.北京:化学工业出版社, 2008.
【2】魏巍, 吴欣强, 柯伟, 等. 接地网材料腐蚀与防护研究进展[J]. 腐蚀科学与防护技术, 2015, 27(3):273-277.
【3】朱忠伟, 吴一平, 葛红花. 变电站接地网腐蚀与防护研究进展[J]. 上海电力学院学报, 2009, 25(6):570-574.
【4】吕旺燕, 刘世念, 苏伟, 等. 变电站接地网腐蚀与防护技术的研究进展[J]. 全面腐蚀控制, 2013, 27(12):26-30.
【5】江培柯. 新型接地材料的腐蚀规律研究[D]. 宜昌:三峡大学, 2021.
【6】徐立. Q235钢、锌和镀锌钢在武汉土壤环境中的腐蚀行为研究[D]. 北京:机械科学研究总院, 2020.
【7】邓盼, 周艺, 朱志平, 等. 接地网材料在土壤中的腐蚀现状及腐蚀机理分析[J]. 广东化工, 2015, 42(4):12-14, 23.
【8】郭安祥, 胡尾娟, 闫爱军, 等. 不锈钢、镀锌钢接地材料在土壤中的腐蚀规律研究[J]. 材料导报, 2015, 29(S2):498-501.
【9】SCULLY J R. Polarization resistance method for determination of instantaneous corrosion rates[J]. Corrosion, 2000, 56(2):199-218.
【10】XIA D H, DENG C M, MACDONALD D, et al. Electrochemical measurements used for assessment of corrosion and protection of metallic materials in the field:a critical review[J]. Journal of Materials Science & Technology, 2022, 112:151-183.
【11】XIA D H, JI Y Y, ZHANG R F, et al. On the localized corrosion of AA5083 in a simulated dynamic seawater/air interface-part 1:corrosion initiation mechanism[J]. Corrosion Science, 2023, 213:110985.
【12】冯南战, 李志忠, 李亨特, 等. 高压变电站接地网的腐蚀防护与监测技术研究进展[J]. 腐蚀科学与防护技术, 2018, 30(3):331-338.
【13】LAW D W, MILLARD S G, BUNGEY J H. Effect of electrode orientation on linear polarisation measurements using sensor controlled guard ring[J]. British Corrosion Journal, 2000, 35(2):136-140.
【14】POURSAEE A, HANSSON C M. Galvanostatic pulse technique with the current confinement guard ring:the laboratory and finite element analysis[J]. Corrosion Science, 2008, 50(10):2739-2746.
【15】寄玉玉, 王佩, 张秀丽, 等. 接地网腐蚀状态原位检测技术研究[J]. 华北电力技术, 2012(8):34-37.
【16】王天正, 徐霞, 郝晋堂, 等. 高压变电站接地网的远程腐蚀监测技术[J]. 腐蚀科学与防护技术, 2016, 28(2):184-188.
【17】黄涛. 变电站接地网材料在模拟土壤中的腐蚀行为研究[D]. 昆明:昆明理工大学, 2014.
【18】曹楚南. 腐蚀电化学原理[M]. 3版.北京:化学工业出版社, 2008.
相关信息