Microstructure of Carburized Layer on Surface of 20MnCr5 Steel Gear
摘 要
在930℃下对20MnCr5钢齿轮进行常规真空渗碳热处理,利用光学显微镜、扫描电镜、透射电镜、电子探针和显微硬度计等研究了渗碳层的显微组织、元素分布和显微硬度。结果表明:渗碳层表层组织由高碳针状马氏体与残余奥氏体组成,随距表面距离增大,针状马氏体向板条马氏体转变;渗碳层中还析出了条状富铬碳化物和球状富锰碳化物,碳化物呈弥散分布;渗碳层表面硬度为860 HV,远高于基体,随距表面距离增大,渗碳层硬度下降。
Abstract
20MnCr5 steel gear was subjected to conventional vacuum carburizing heat treatment at 930℃. The microstructure, element distribution and microhardness of the carburized layer were studied by optical microscope, scanning electron microscope, transmission electron microscope, electron probe and microhardness tester. The results show that the microstructure of the carburized layer surface layer consisted of high-carbon acicular martensite and residual austenite. With increasing the distance from the surface, the acicular martensite changed to lath martensite. Strip-like chromium-rich carbides and spherical manganese-rich carbides were also precipitated in the carburized layer, and the carbides were dispersed. The surface hardness of the carburized layer was 860 HV, which was much higher than that of the substrate. With increasing the distance from the surface, the hardness of the carburized layer decreased.
中图分类号 TG156.8 DOI 10.11973/jxgccl202309018
所属栏目 专题报道(金属材料表面处理)
基金项目
收稿日期 2022/11/30
修改稿日期 2023/8/21
网络出版日期
作者单位点击查看
备注王强(1994-),男,上海人,工程师,硕士
引用该论文: WANG Qiang,ZHAO Sixin,GAO Jiaqiang. Microstructure of Carburized Layer on Surface of 20MnCr5 Steel Gear[J]. Materials for mechancial engineering, 2023, 47(9): 106~110
王强,赵四新,高加强. 20MnCr5钢齿轮表面渗碳层的显微组织[J]. 机械工程材料, 2023, 47(9): 106~110
共有人对该论文发表了看法,其中:
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】李茂林, 郭德朋, 焦殿辉, 等.汽车用齿轮钢国内外概述及其发展趋势[J].现代制造技术与装备, 2013(4):13-16. LI M L, GUO D P, JIAO D H, et al.Overview of automobile gear steel at home and abroad and its development trend[J].Modern Manufacturing Technology and Equipment, 2013(4):13-16.
【2】王洪, 李光瑾, 陈德华, 等.20CrMnMo钢不同渗碳淬硬层深度的组织与应力分布[J].上海金属, 2012, 34(1):10-14. WANG H, LI G J, CHEN D H, et al.Microstructure and stress distribution characteristics of 20CrMnMo steel with different depths of carburized layer[J].Shanghai Metals, 2012, 34(1):10-14.
【3】陈晖, 周细应.汽车齿轮热处理工艺的研究进展[J].材料导报, 2010, 24(13):93-96. CHEN H, ZHOU X Y.Review and progress of heat treatment process for automobile gear[J].Materials Reports, 2010, 24(13):93-96.
【4】NOJIMA K, OGATA K, TANAKA M, et al.Bending fatigue strength of case-carburized helical gears (in the case of large helix angles)[J].Journal of Mechanical Science and Technology, 2017, 31(12):5657-5663.
【5】JO B, SHARIFIMEHR S, SHIM Y B, et al.Cyclic deformation and fatigue behavior of carburized automotive gear steel and predictions including multiaxial stress states[J].International Journal of Fatigue, 2017, 100:454-465.
【6】李阳, 侯圣文, 贺尔康, 等.20MnCr5齿轮钢渗碳层弥散碳化物形成机理[J].金属热处理, 2022, 47(12):196-200. LI Y, HOU S W, HE E K, et al.Formation mechanism of dispersed carbide in carburized case of 20MnCr5 gear steel[J].Heat Treatment of Metals, 2022, 47(12):196-200.
【7】高金柱, 顾敏, 王爱香, 等.常用典型齿轮钢渗碳层的组织与性能[J].机械工程材料, 2012, 36(2):49-51. GAO J Z, GU M, WANG A X, et al.Microstructure and property of carbonization layer in common and typical gear steels[J].Materials for Mechanical Engineering, 2012, 36(2):49-51.
【8】MIAO S, WANG J G, JU D Y, et al.Improvement and analysis of fatigue strength for mild steel 20MnCrS5 during carburizing and quenching[J].Materials Science, 2020, 26(2):192-198.
【9】申景霞, 郑艳, 张海霞, 等.含硫齿轮钢20CrMnTiH中硫化物对切削性能的影响[J].特殊钢, 2012, 33(3):47-49. SHEN J X, ZHENG Y, ZHANG H X, et al.Effect of sulphide on cutting characteristics of sulphur bearing gear steel 20CrMnTiH[J].Special Steel, 2012, 33(3):47-49.
【10】STORMVINTER A, MIYAMOTO G, FURUHARA T, et al.Effect of carbon content on variant pairing of martensite in Fe-C alloys[J].Acta Materialia, 2012, 60(20):7265-7274.
【11】吴承建. 金属材料学[M]. 北京:冶金工业出版社, 2014:42-49. WU C J. Metal material science[M]. Beijing:Metallurgical Industry Press, 2014:42-49.
【12】马森林, 高文栋, 沈玉明.ECM低压真空渗碳技术应用研究与探讨[J].汽车工艺与材料, 2004(8):27-30. MA S L, GAO W D, SHEN Y M.Application researches and discussion on ECM low pressure vacuum carburizing technology[J].Automobile Technology & Material, 2004(8):27-30.
【13】孙振淋, 张茜, 辛玉武, 等.渗碳方式对18CrNi4A钢齿轮渗层的影响[J].金属热处理, 2015, 40(12):128-131. SUN Z L, ZHANG Q, XIN Y W, et al.Effect of carburizing method on carburized layer of 18CrNi4A steel gear[J].Heat Treatment of Metals, 2015, 40(12):128-131.
【14】王慧君.35CrMo钢渗碳及等温淬火的组织与性能及其应用[J].上海金属, 1993, 15(2):32-36. WANG H J.Study on the microstructures and properties of 35CrMo steel after carburizing and isothermal quenching and its application[J].Shanghai Metals, 1993, 15(2):32-36.
【2】王洪, 李光瑾, 陈德华, 等.20CrMnMo钢不同渗碳淬硬层深度的组织与应力分布[J].上海金属, 2012, 34(1):10-14. WANG H, LI G J, CHEN D H, et al.Microstructure and stress distribution characteristics of 20CrMnMo steel with different depths of carburized layer[J].Shanghai Metals, 2012, 34(1):10-14.
【3】陈晖, 周细应.汽车齿轮热处理工艺的研究进展[J].材料导报, 2010, 24(13):93-96. CHEN H, ZHOU X Y.Review and progress of heat treatment process for automobile gear[J].Materials Reports, 2010, 24(13):93-96.
【4】NOJIMA K, OGATA K, TANAKA M, et al.Bending fatigue strength of case-carburized helical gears (in the case of large helix angles)[J].Journal of Mechanical Science and Technology, 2017, 31(12):5657-5663.
【5】JO B, SHARIFIMEHR S, SHIM Y B, et al.Cyclic deformation and fatigue behavior of carburized automotive gear steel and predictions including multiaxial stress states[J].International Journal of Fatigue, 2017, 100:454-465.
【6】李阳, 侯圣文, 贺尔康, 等.20MnCr5齿轮钢渗碳层弥散碳化物形成机理[J].金属热处理, 2022, 47(12):196-200. LI Y, HOU S W, HE E K, et al.Formation mechanism of dispersed carbide in carburized case of 20MnCr5 gear steel[J].Heat Treatment of Metals, 2022, 47(12):196-200.
【7】高金柱, 顾敏, 王爱香, 等.常用典型齿轮钢渗碳层的组织与性能[J].机械工程材料, 2012, 36(2):49-51. GAO J Z, GU M, WANG A X, et al.Microstructure and property of carbonization layer in common and typical gear steels[J].Materials for Mechanical Engineering, 2012, 36(2):49-51.
【8】MIAO S, WANG J G, JU D Y, et al.Improvement and analysis of fatigue strength for mild steel 20MnCrS5 during carburizing and quenching[J].Materials Science, 2020, 26(2):192-198.
【9】申景霞, 郑艳, 张海霞, 等.含硫齿轮钢20CrMnTiH中硫化物对切削性能的影响[J].特殊钢, 2012, 33(3):47-49. SHEN J X, ZHENG Y, ZHANG H X, et al.Effect of sulphide on cutting characteristics of sulphur bearing gear steel 20CrMnTiH[J].Special Steel, 2012, 33(3):47-49.
【10】STORMVINTER A, MIYAMOTO G, FURUHARA T, et al.Effect of carbon content on variant pairing of martensite in Fe-C alloys[J].Acta Materialia, 2012, 60(20):7265-7274.
【11】吴承建. 金属材料学[M]. 北京:冶金工业出版社, 2014:42-49. WU C J. Metal material science[M]. Beijing:Metallurgical Industry Press, 2014:42-49.
【12】马森林, 高文栋, 沈玉明.ECM低压真空渗碳技术应用研究与探讨[J].汽车工艺与材料, 2004(8):27-30. MA S L, GAO W D, SHEN Y M.Application researches and discussion on ECM low pressure vacuum carburizing technology[J].Automobile Technology & Material, 2004(8):27-30.
【13】孙振淋, 张茜, 辛玉武, 等.渗碳方式对18CrNi4A钢齿轮渗层的影响[J].金属热处理, 2015, 40(12):128-131. SUN Z L, ZHANG Q, XIN Y W, et al.Effect of carburizing method on carburized layer of 18CrNi4A steel gear[J].Heat Treatment of Metals, 2015, 40(12):128-131.
【14】王慧君.35CrMo钢渗碳及等温淬火的组织与性能及其应用[J].上海金属, 1993, 15(2):32-36. WANG H J.Study on the microstructures and properties of 35CrMo steel after carburizing and isothermal quenching and its application[J].Shanghai Metals, 1993, 15(2):32-36.
相关信息