St52-3铸钢非正常正火的组织和性能
ABNORMAL NORMALIZING MICROSTRUCTURE AND MECHAMICAL PROPERTIES OF St52-3 CAST STEEL
摘 要
采用化学分析、力学性能测试、断口扫描、硬度测定和金相检验方法对St52-3铸钢正火形成的非正常组织进行了分析。结果表明,St52-3铸钢正火温度低形成的残留铸态组织为粗大的黑色珠光体网和大晶粒内部的针状铁素体。此类非正常正火组织钢的冲击功很低,脆性很大。
铸钢
冲击功
Microstructure of abnormal normalizing
Cast steel
Impact work
Abstract
By means of chemical analysis,mechanical properties testing,scanning electron microscopy,hardness test and metallography,the microstructure of abnormal normalizing of St52-3 cast steel were analysised. The results showed that there were black pearlite nets and needle ferrite in the coarse grains of the St52-3 cast steel after low temperature normalizing,which had much low impact and high brittleness.
中图分类号 TG142.1
所属栏目 试验与研究
基金项目
收稿日期 2006/3/31
修改稿日期
网络出版日期
作者单位点击查看
备注白培谦(1965-),男,高级工程师,工学学士。
引用该论文: BAI Pei-qian. ABNORMAL NORMALIZING MICROSTRUCTURE AND MECHAMICAL PROPERTIES OF St52-3 CAST STEEL[J]. Physical Testing and Chemical Analysis part A:Physical Testing, 2007, 43(12): 608～610
白培谦. St52-3铸钢非正常正火的组织和性能[J]. 理化检验－物理分册, 2007, 43(12): 608～610
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献
【1】上海市机械制造工艺研究所.金相分析技术［M］.上海:上海科学技术文献出版社,1987:682．
【2】任颂赞.钢铁金相图谱［M］.上海:上海科学技术文献出版社,2003:94．
【3】美国金属学会.金属手册［M］.北京:机械工业出版社,1986:464．
【2】任颂赞.钢铁金相图谱［M］.上海:上海科学技术文献出版社,2003:94．
【3】美国金属学会.金属手册［M］.北京:机械工业出版社,1986:464．
相关信息