Degradation Mechanism and Mitigation Measures of Key Parts of ПГВ-1000 Horizontal Steam Generator in Operation

YU Ziqun

doi:10.11973/fsyfh-201910010

Corrosion & Protection > 2019 > 40(10): 764-770,776. > DOI: 10.11973/fsyfh-201910010

YU Ziqun. Degradation Mechanism and Mitigation Measures of Key Parts of ПГВ-1000 Horizontal Steam Generator in Operation[J]. Corrosion & Protection, 2019, 40(10): 764-770,776. DOI: 10.11973/fsyfh-201910010

Citation:

PDF (1573 KB)

Degradation Mechanism and Mitigation Measures of Key Parts of ПГВ-1000 Horizontal Steam Generator in Operation

YU Ziqun^,

CNNP Jiangsu Nuclear Power Company Limited, Lianyungang 222042, China

More Information

Received Date: September 28, 2018

Graphical Abstract

Abstract

Abstract

The degradation mechanism of key parts of ПГВ-1000 horizontal steam generator in operation for several WWER-1000 units in Russia, Ukraine and Bulgaria are tracked and studied for a long time. The damage problems in the contact zone of punched area of cold collecting pipe and the 111 welded joint between collecting pipe and casing connecting section are collated and analyzed. And several improvements, mitigation and supervision measures are proposed to provide reference for the operation and aging management of the same type of horizontal steam generator in domestic WWER units or other facilities.
- horizontal steam generator,
- primary coolant collector,
- degradation mechanism,
- mitigation measure

FullText(HTML)

References (13)

References

[1]	IAEA. WWER-1000 steam generator integrity:IAEA-EBP-WWER-07[R].Vienna:International Atomic Agency,1997.
[2]	Иванович Л В. Расчетно-экспериментальный анализ влияния термосиловых воздействий наповреждение узла приварки коллектора теплоносителя к корпусу парогенератора ПГВ-1000М[D]. Moscow:НИУ МЭИ,2015.
[3]	IAEA. Assessment and management of ageing of major nuclear power plant components important to safety:steam generators:IAEA-TECDOC-1668[R]. Vienna:International Atomic Agency,2011.
[4]	FSUE EDO "GIDROPRESS". Steam Generator ПГВ-1000М Assembly Drawing 428M.05.01СБ[Z]. Podolck:FSUE EDO "GIDROPRESS",2013.
[5]	ХАРЧЕНКО С А, ЖУКОВ Р Ю,КУРДИН М Е,et al. Оценка эффективности мероприятий по предотвращению повреждений сварных швов №111на парогенераторах АЭС с ВВЭР-1000[C/OL]//the 9th International Conference "Safety Assurance of NPP with WWER ". Podolck:FSUE EDO GIDROPRESS,2015[2018-09-29]. http://www.gidropress.podolsk.ru/files/proceedings/mntk2015/autorun/article148-ru.htm.
[6]	ДУБ А В, ДУРЫНИН В А, РАЗЫГРАЕВ А Н,et al. Разработка методик ультразвукового контроля и определения работоспособности узла приварки коллектора к парогенератору ПГВ-1000М[J]. Technical Diagnosis and Nondestructive Testing,2014(4):36-51.
[7]	НЕКЛЮДОВ И М,ОЖИГОВ Л С,МИТРОФАНОВ А С, et al. Механизм повреждений сварных соединений приварки коллекторов к корпусам парогенераторов энергоблоков ВВЭР-1000[J]. Problems of Atomic Science and Technology,2012,78(2):40-45.
[8]	КАЗАНЦЕВ А Г, ЛОВЧЕВ В Н, ГУЦЕВ Д Ф, et al. Критерии инициации и развития коррозионных повреждений в узле приварки коллектора теплоносителя к корпусу парогенератора ПГВ-1000ВВЭР[C/OL]//the 8th International Conference "Safety Assurance of NPP with WWER". Podolck:FSUE, EDO GIDROPRESS, 2013[2018-09-29]. http://www.gidropress.podolsk.ru/files/proceedings/mntk2013/autorun/article187-ru.htm.
[9]	MATOCHA1 K, í EK P, KANDER L,et al. Resistance of 10GN2MFA-a low alloy steel to stress corrosion cracking in high temperature water[C]//Nuclear Power Control, Reliability and Human Factors. Croatia:InTech,2011:275-286.
[10]	ЛЯКИШЕВ С Л, ХАРЧЕНКО С А, КУЧЕРЯВЧЕНКОВ А В,et al. Оптимизация конструкции узла приварки коллектора к корпусу парогенератора[C/OL]//The 7th International Seminar on Horizontal Steam Generators. Podolck:FSUE EDO GIDROPRESS,2007[2018-09-29]. http://www.gidropress.podolsk.ru/files/proceedings/seminar7/documents/f65.pdf.
[11]	ПОДРЕЗОВ Н Н,ТОМИЛИН С А, ШИШОВ В В. Повышение эксплуатационной надежности сварных соединений парогенераторов для реакторных установок на основе ВВЭР[J]. Global Nuclear Safety,2016,21(4):22-26.
[12]	Правила Контроля Основного Металла, Сварных Соединений и Наплавленных Поверхностей при Эксплуатации Оборудования,Трубопроводов и Других Элементов Атомных Станций:НП-084-15[S]. Moscow:ФБУ НТЦ ЯРБ,2016.
[13]	СТАРЧЕНКО Е Г, КАЗАНЦЕВ А Г, ХОДАКОВ В Д, et al. Обоснование увеличения допустимого времени суммарной термообработки после ремонта сварных соединений оборудования аэс из стали 10ГН2МФА[C/OL]//the 5th International Conference "Safety Assurance of NPP with WWER". Podolck:FSUE EDO GIDROPRESS,2007[2018-09-29]. http://www.gidropress.podolsk.ru/files/proceedings/mntk2007/disc/documents/f35.pdf.

Cited By

Get Citation

PDF

XML

Article views (8) PDF downloads (3)

Turn off MathJax

Article Contents

Abstract

References

Degradation Mechanism and Mitigation Measures of Key Parts of ПГВ-1000 Horizontal Steam Generator in Operation

Abstract

References

Catalog

Export File

Citation

Format

Content