Induction Mechanism and Evolution Process of Cavitation in Expander Impeller

More Information
  • Received Date: September 05, 2021
  • The pressure fluctuation range in the flow field environment of the expander impeller was determined by numerical simulation. The corrosion tests of different time were carried out for impeller material of FV520B-S steel in the simulated working environment of gas flow field in expander using a high temperature and high pressure reactor. Then the electrochemical properties and corrosion morphology of the FV520B-S steel after corrosion were analyzed by electrochemical test and scanning electron microscopy, and the induction and evolution of cavitation in impeller were studied. The results showed that at the beginning of the experiment the passivation film on the surface of the FV520B-S steel had a good protection to the substrate, so there were no obvious pits on the substrate surface. After corrosion for 6 days, the formation and rupture of bubbles on the metal surface led to the destruction of the passivation film, so obvious cavitation pits appeared on the metal surface. Under continuous cavitation, the FV520B-S steel exhibited an activated corrosion characteristic. The corrosion process changed from anode control to cathode control. Therefore, the cavitation characteristics of the impeller were the result of the destruction of passivation film and the action of oxygen diffusion.
  • [1]
    刘鸿德. 透平膨胀机的关键控制技术研究[D].杭州:杭州电子科技大学,2017.
    [2]
    闫静文, 杨柯峰,侯佳,等.有机朗肯循环膨胀机的研究进展和应用现状[J].热力发电,2019,48(7):10-18.
    [3]
    REVEL P,KIRCHER D,BOGARD V.Experimental and numerical simulation of a stainless steel coating subjected to thermal fatigue[J].Materials Science and Engineering:A,2000,290(1/2):25-32.
    [4]
    CABRINI M,LORENZI S,PASTORE T,et al.Materials selection for dew-point corrosion in geothermal fluids containing acid chloride[J].Geothermics,2017,69:139-144.
    [5]
    BASHIR A,DUDZI AN'G SKI W,DUDZI AN'G SKI M,et al.Corrosion fatigue crack propagation rates for steam turbine blade 13% Cr steels[J].Solid State Phenomena,2015,227:7-10.
    [6]
    彭岳峰, 徐柱,吴小亮,等.海水升压泵泵轴腐蚀失效分析[J].金属热处理,2019,44(S1):384-387.
    [7]
    余仁强, 何建军,李微,等.火电厂循环泵叶轮材料Cr30A在脱硫浆液腐蚀环境中的交互损伤失效行为研究[J].中国腐蚀与防护学报,2019,39(4):353-358.
    [8]
    杜兆伟, 李华峰,伍志明,等.某船海水泵叶轮失效原因分析[J].材料保护,2019,52(6):179-183.
    [9]
    XU D,HUANG W,RUSCHAU G,et al.Laboratory investigation of MIC threat due to hydrotest using untreated seawater and subsequent exposure to pipeline fluids with and without SRB spiking[J].Engineering Failure Analysis,2013,28:149-159.
    [10]
    NEŠIĆ S.Key issues related to modelling of internal corrosion of oil and gas pipelines-A review[J].Corrosion Science,2007,49(12):4308-4338.
    [11]
    PHILIPPE L V S,LYON S B,SAMMON C,et al.Validation of electrochemical impedance measurements for water sorption into epoxy coatings using gravimetry and infra-red spectroscopy[J].Corrosion Science,2008,50(3):887-896.
    [12]
    JADHAV N,GELLING V J.Review-the use of localized electrochemical techniques for corrosion studies[J].Journal of the Electrochemical Society,2019,166(11):C3461-C3476.
    [13]
    CÁCERES L,VARGAS T,HERRERA L.Influence of pitting and iron oxide formation during corrosion of carbon steel in unbuffered NaCl solutions[J].Corrosion Science,2009,51(5):971-978.
    [14]
    CAERES L, VARGAS T, PARRA M. Study of the variational carbon steel as a function of dissolved oxygen and NaCl patterns for corrosion kinetics of concentration[J]. Electrochimica Acta, 2009, 54:7435-7443.
    [15]
    HOSEINIEH S M,HOMBORG A M,SHAHRABI T,et al.A novel approach for the evaluation of under deposit corrosion in marine environments using combined analysis by electrochemical impedance spectroscopy and electrochemical noise[J].Electrochimica Acta,2016,217:226-241.
    [16]
    HIRSCHORN B,ORAZEM M E,TRIBOLLET B,et al.Determination of effective capacitance and film thickness from constant-phase-element parameters[J].Electrochimica Acta,2010,55(21):6218-6227.
  • Cited by

    Periodical cited type(1)

    1. 邓立军. 屋面冷却泵气蚀现象的分析与处理. 建筑施工. 2024(01): 129-131 .

    Other cited types(0)

Catalog

    Article views (10) PDF downloads (6) Cited by(1)

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return