Citation: | YAN Fuhua, ZHANG Yue, FAN Weigang, ZHANG Yamei, FENG Dan. Corrosion Behavior of Aluminum Silicon Alloy in Marine Environment[J]. Corrosion & Protection, 2024, 45(10): 65-67. DOI: 10.11973/fsyfh220454 |
The corrosion behavior of aluminum silicon alloy in marine environment was studied using scanning electron microscope and energy dispersive spectrometer. The results indicate that the pinholes and eutectic silicon aggregation areas in aluminum silicon alloys preferentially underwent pitting, with corrosion extending along the aluminum silicon interface and grain boundaries, ultimately developing into large-scale overall corrosion.
[1] |
李丽, 苏霄. 1050A铝合金模拟海洋大气环境腐蚀行为的中性盐雾试验 [J]. 腐蚀与防护, 2014, 35(4):367-370,386.
LI L, SU X. Corrosion behavior of aluminum alloy 1050A during cyclic wet-dry immersion test in simulated marine atmospheric environment [J]. Corrosion & Protection, 2014, 35(4):367-370,386.
|
[2] |
范鹏铸造Al-Si系合金电化学行为的研究南宁广西大学2007范鹏. 铸造Al-Si系合金电化学行为的研究 [D]. 南宁: 广西大学, 2007.
FAN PStudy on electrochemical behavior of cast Al-Si alloyNanningGuangxi University2007FAN P. Study on electrochemical behavior of cast Al-Si alloy [D]. Nanning: Guangxi University, 2007.
|
[3] |
安勇良, 刘明明, 尹冬松, 等. Al-Si合金在模拟海水中的腐蚀行为 [J]. 黑龙江科技大学学报, 2018, 28(6):678-681.
AN Y L, LIU M M, YIN D S, et al. Corrosion behavior of Al-Si alloy in simulated seawater [J]. Journal of Heilongjiang University of Science and Technology, 2018, 28(6):678-681.
|