YANG Genquan, ZHANG Zhi, HU Lihua, WANG Zhiguo, CHEN Dajiang. Corrosion Causes and Control Measures of Uninsulated Subsea Pipeline for Oil, Gas and Water Transport[J]. Corrosion & Protection, 2024, 45(9): 120-125. DOI: 10.11973/fsyfh220458
Citation: YANG Genquan, ZHANG Zhi, HU Lihua, WANG Zhiguo, CHEN Dajiang. Corrosion Causes and Control Measures of Uninsulated Subsea Pipeline for Oil, Gas and Water Transport[J]. Corrosion & Protection, 2024, 45(9): 120-125. DOI: 10.11973/fsyfh220458

Corrosion Causes and Control Measures of Uninsulated Subsea Pipeline for Oil, Gas and Water Transport

More Information
  • Received Date: July 28, 2022
  • The intelligent internal inspection show that many corrosion defects were found in the front and middle sections of an oil, gas and water mixed transportation uninsulated subsea pipeline. The corrosion causes of the subsea pipeline were analyzed by simulated corrosion experiment, pigging products and microbial test analysis, and temperature change curve analysis. The results show that a lot of number of corrosion defects in the front and middle sections of the pipeline were caused by the interaction between SRB and TGB which induced corrosion and underdeposit corrosion. The different locations of the defects in the subsea pipeline at different time were caused by temperature drop along with pipeline because of the change in the inlet temperature. In recent years, measures such as adding pigging, adjusting the injection of bactericide and monitoring the effect of bactericide have been taken, the corrosion of subsea pipeline has been alleviated, and the corrosion has not accelerated significantly.

  • [1]
    DANIEL PIntegrity management for piggable and non-piggable subsea pipelinesCorrosion 2008New OrleansNACE Conference200808135DANIEL P. Integrity management for piggable and non-piggable subsea pipelines [C]//Corrosion 2008. New Orleans: NACE Conference, 2008: 08135.
    [2]
    胡丽华, 常炜, 张雷, 等. X65钢和3Cr钢作为海底管道用钢抗CO2腐蚀性能研究[J]. 中国海上油气, 2011, 23(2):131-134.

    HU L H, CHANG W, ZHANG L, et al. Research on the CO2 corrosion resistance of X65 and 3Cr steels applied to subsea pipeline[J]. China Offshore Oil and Gas, 2011, 23(2):131-134.
    [3]
    龙凤乐, 郑文军, 陈长风, 等. 温度、CO2分压、流速、pH值对X65管线钢CO2均匀腐蚀速率的影响规律[J]. 腐蚀与防护, 2005, 26(7):290-293,286.

    LONG F L, ZHENG W J, CHEN C F, et al. Influence of temperature, CO2 partial pressure, flow rate and pH value on uniform corrosion rate of X65 pipeline steel[J]. Corrosion & Protection, 2005, 26(7):290-293,286.
    [4]
    胡丽华, 常炜, 余晓毅, 等. CO2分压对碳钢海底管道CO2/H2S腐蚀的影响[J]. 表面技术, 2016, 45(5):56-61.

    HU L H, CHANG W, YU X Y, et al. Effect of partial pressure of CO2 on corrosion of carbon steel subsea pipeline in CO2/H2S environment[J]. Surface Technology, 2016, 45(5):56-61.
    [5]
    李鑫, 尚东芝, 于浩波, 等. 油气管道SRB腐蚀研究新进展[J]. 表面技术, 2021, 50(2):211-220.

    LI X, SHANG D Z, YU H B, et al. Research progress on oil & gas pipeline corrosion induced by SRB[J]. Surface Technology, 2021, 50(2):211-220.
    [6]
    POWELL D, EINER R, CHEEK J, et alPractical experience in re-establishing control over SRBs and bacteria generated H2S in subsea pipelines following hurricane ikeCorrosion 2010TexasNACE2010POWELL D, EINER R, CHEEK J, et al. Practical experience in re-establishing control over SRBs and bacteria generated H2S in subsea pipelines following hurricane ike[C]//Corrosion 2010. Texas: NACE, 2010.
    [7]
    张润杰, 曹振恒, 张贵雄, 等. SRB对油气管道腐蚀影响的研究进展[J]. 腐蚀与防护, 2021, 42(10):68-73,108.

    ZHANG R J, CAO Z H, ZHANG G X, et al. Research progress of SRB effect on corrosion of oil and gas pipelines[J]. Corrosion & Protection, 2021, 42(10):68-73,108.
    [8]
    KATO S. Microbial extracellular electron transfer and its relevance to iron corrosion[J]. Microbial Biotechnology, 2016, 9(2):141-148.
    [9]
    XUE H B, CHENG F Y, ZHU Z J, et alInternal pitting corrosion of X80 pipeline steel under deposited sand bed in CO2-saturated solutionsCorrosion 2011HoustonNACE201111264XUE H B, CHENG F Y, ZHU Z J, et al. Internal pitting corrosion of X80 pipeline steel under deposited sand bed in CO2-saturated solutions[C]//Corrosion 2011. Houston: NACE, 2011: 11264.
    [10]
    STANDLEE S, EFIRD K D, SPILLER DUnder deposit corrosion from iron sulfideCorrosion 2011HoustonNACE201111266STANDLEE S, EFIRD K D, SPILLER D. Under deposit corrosion from iron sulfide[C]//Corrosion 2011. Houston: NACE, 2011: 11266.
    [11]
    AL-SULAIMAN S, AL-MITHIN A, AL-SHAMARI A, et alMicrobiologically influenced corrosion of a crude oil pipelineCorrosion 2011HoustonNACE201110210AL-SULAIMAN S, AL-MITHIN A, AL-SHAMARI A, et al. Microbiologically influenced corrosion of a crude oil pipeline[C]//Corrosion 2011. Houston: NACE, 2011: 10210.
    [12]
    GU T, XU D KDemystifying mic mechanismsCorrosion 2010TexasNACE2010GU T, XU D K. Demystifying mic mechanisms[C]//Corrosion 2010. Texas: NACE, 2010.

Catalog

    Article views (42) PDF downloads (25) Cited by()

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return