BA Fa-hai, XUE Yu. Failure Analysis of Crane Wire Rope Fracture[J]. Materials and Mechanical Engineering, 2016, 40(8): 103-106. DOI: 10.11973/jxgccl201608024
Citation: BA Fa-hai, XUE Yu. Failure Analysis of Crane Wire Rope Fracture[J]. Materials and Mechanical Engineering, 2016, 40(8): 103-106. DOI: 10.11973/jxgccl201608024

Failure Analysis of Crane Wire Rope Fracture

More Information
  • Received Date: June 21, 2016
  • The fracture failure of the crane wire rope was analyzed by the methods of macroscopic examination, chemical composition analysis, mechanical property test, fracture analysis, metallographic examination and so on. The results show that the fracture of the wire rope was ductile. The wire rope sustained a serious extrusion and friction during use, leading to the wire damage and transformation hardening by the produced high temperature. The damage and transformation hardening caused the decrease of cross sectional area and reduced the bearing power of the wire, resulting in the wire broken and the wire rope overload fracture.
  • [1]
    张德英,单联敏.钢丝绳使用中断丝原因分析[J].金属制品, 1999, 25(3): 7-9.
    [2]
    肖永清.起重钢丝绳的失效分析与安全使用[J].金属制品, 2010, 36(6): 63-67.
    [3]
    王新华,江爱华,高海生,等.通用桥式起重机钢丝绳断裂失效分析[J].理化检验-物理分册, 2012, 48(4): 269-273.
    [4]
    汪浩.提升钢丝绳的损坏原因及防护措施[J].煤矿机械, 2008, 29(1): 141-144.
    [5]
    王强. 起重机用钢丝绳的损伤形式及防治措施[J]. 港口装卸, 2007(1): 13-17.

Catalog

    Article views (22) PDF downloads (2) Cited by()

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return