SONG Tijie, YU Yanyan, LIU Chunmi, SONG Xue, KANG Kai, WANG Lin, SUN Mengmeng. Fracture Reason of G95Cr18 Stainless Steel Joint Bearing Outer Ring[J]. Materials and Mechanical Engineering, 2025, 49(1): 112-119. DOI: 10.11973/jxgccl240497
Citation: SONG Tijie, YU Yanyan, LIU Chunmi, SONG Xue, KANG Kai, WANG Lin, SUN Mengmeng. Fracture Reason of G95Cr18 Stainless Steel Joint Bearing Outer Ring[J]. Materials and Mechanical Engineering, 2025, 49(1): 112-119. DOI: 10.11973/jxgccl240497

Fracture Reason of G95Cr18 Stainless Steel Joint Bearing Outer Ring

More Information
  • Received Date: October 16, 2024
  • Revised Date: November 28, 2024
  • A joint bearing outer ring placed in the connecting rod mounting hole by interference fit broke. Combined with bearing structure and material properties, the fracture mode and cause of the outer ring were analyzed by field investigation, fracture macro and micro morphology observation, microstructure analysis, hardness test and finite element simulation. The results show that the fracture mode of the joint bearing outer ring was one time overload fracture. Cracks occurred at the mounting notch of the bearing outer ring under the action of applied load. At the same time, due to the low hardness, local materials on the edge notch fell off into the bearing friction pair, causing abrasive wear and swing stuck, and the occurrence of swing stuck made the outer ring gradually slipped out of the mounting hole, as a result, the tendency of one time overload fracture increased and the outer ring fracture was eventually caused.

  • [1]
    刘云帆,秦红玲,韩翠红,等. 自润滑关节轴承寿命试验及损伤失效机理研究现状[J]. 材料导报,2021(1):36-45.

    LIU Y F ,QIN H L ,HAN C H ,et al. Research status of life test and damage failure mechanism of self-lubricating joint bearings[J]. Materials Reports,2021(1):36-45.
    [2]
    黄雄荣. 自润滑关节轴承在不同应力下的摩擦磨损特性[J]. 航空材料学报,2024,44(3):132-141.

    HUANG X R. Friction and wear characteristics of self-lubricating joint bearing under different stresses[J]. Journal of Aeronautical Materials,2024,44(3):132-141.
    [3]
    杨碧真. 某重型越野车用球头杆端关节轴承开发[J]. 科技与创新,2024(11):44-47.

    YANG B Z. Development of spherical joint bearing for a heavy off-road vehicle[J]. Science and Technology and Innovation,2024(11):44-47.
    [4]
    甘武平. 动车组轴箱轴承失效原因及预防措施[J]. 轨道交通装备与技术,2024,32(4):29-32.

    GAN W P. Failure causes and preventive measures of axle box bearings of EMU[J]. Rail Transportation Equipment and Technology,2024,32(4):29-32.
    [5]
    李付伟. 高压气淬后9Cr18钢的组织和性能[J]. 热处理技术与装备,2018,39(2):41-43.

    LI F W. Microstructure and properties of 9Cr18 steel after high pressure gas quenching[J]. Heat Treatment Technology and Equipment,2018,39(2):41-43.
    [6]
    熊雯,蔡海斌,夏军,等. 轴承断裂材料的微观检测及有限元分析[J]. 武汉工程职业技术学院学报,2019,31(4):18-22.

    XIONG W ,CAI H B ,XIA J ,et al. Microscopic detection and fracture finite element analysis of bearing fracture materials[J]. Journal of Wuhan Engineering Institute,2019,31(4):18-22.
    [7]
    穆晓彪,邵洙浩,郝春辉,等. 谐波减速器柔轮与柔性轴承断裂失效分析[J]. 机械传动,2023,47(3):100-104.

    MU X B ,SHAO Z H ,HAO C H ,et al. Fracture analysis on flexspline and flexible bearing of the harmonic reducer[J]. Journal of Mechanical Transmission,2023,47(3):100-104.
    [8]
    王宇石,邱宝象,铁晓艳,等. 某型圆锥滚子轴承保持架断裂仿真分析[J]. 轴承,2017(7):11-17.

    WANG Y S ,QIU B X ,TIE X Y ,et al. Simulation analysis on fracture of cage in a certain type of tapered roller bearing[J]. Bearing,2017(7):11-17.
    [9]
    孙晗. 某变速箱用内圈单挡边圆柱滚子轴承疲劳断裂失效分析[J]. 哈尔滨轴承,2024,45(1):37-40.

    SUN H. Fatigue fracture analysis of a cylindrical roller bearing with single rib on inner ring used in gearbox[J]. Journal of Harbin Bearing,2024,45(1):37-40.
    [10]
    董晨,屈伸,李天夫,等. 航空发动机轴承烧伤失效分析[J/OL]. 热加工工艺,1-6[2024-08-21]. http://doi.org/10.14158/j.cnki.1001-3814.20222349.

    DONG C ,QU X ,LI T F ,et al. Analysis of aero engine bearing burn failure[J/OL]. Hot Working Technology,1-6[2024-08-21]. http://doi.org/10.14158/j.cnki.1001-3814.20222349.
    [11]
    张李锋,段江. 750 kV变电站地刀连杆杆端轴承断裂失效分析[J]. 材料导报,2019,33(增刊2):452-454.

    ZHANG L F ,DUAN J. Fracture failure analysis of ground cutter connecting rod end bearing in 750 kV substation[J]. Materials Review,2019,33(S2):452-454.
    [12]
    曾坤,张韶佳,陈昕,等. 杆端关节轴承失效分析[J]. 失效分析与预防,2018,13(5):318-323.

    ZENG K ,ZHANG S J ,CHEN X ,et al. Failure analysis of rod end joint bearing[J]. Failure Analysis and Prevention,2018,13(5):318-323.
    [13]
    马春山,吴进军. 关节轴承磨损失效的研究现状及进展[J]. 内燃机与配件,2018(18):90-91.

    MA C S ,WU J J. Research status and progress of wear failure of joint bearings[J]. Internal Combustion Engine and Parts,2018(18):90-91.
    [14]
    吴玫,闫佳山,金贺. 关节轴承外圈装配缺口加工工艺分析[J]. 轴承,2022(1):44-46.

    WU M ,YAN J S ,JIN H. Processing technology analysis of assembly Notch of outer ring of joint bearing[J]. Bearing,2022(1):44-46.
    [15]
    安敏,付中元,袁超,等. 淬火后清洗和冷处理工艺对9Cr18钢轴承套圈残留奥氏体含量的影响[J]. 金属热处理,2021,46(6):21-24.

    AN M ,FU Z Y ,YUAN C ,et al. Effects of post-quenching cleaning and cold treatment process on retained austenite content of 9Cr18 steel bearing ring[J]. Heat Treatment of Metals,2021,46(6):21-24.

Catalog

    Article views (20) PDF downloads (20) Cited by()

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return