WANG Haitao, GAO Xingjian. Cause Analysis on Surface Cracks of X52 Pipe Line Steel Hot-Rolling Coils[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2018, 54(3): 226-228,232. DOI: 10.11973/lhjy-wl201803015
Citation: WANG Haitao, GAO Xingjian. Cause Analysis on Surface Cracks of X52 Pipe Line Steel Hot-Rolling Coils[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2018, 54(3): 226-228,232. DOI: 10.11973/lhjy-wl201803015

Cause Analysis on Surface Cracks of X52 Pipe Line Steel Hot-Rolling Coils

More Information
  • Received Date: November 07, 2017
  • Surface crack defect were observed on the tail of X52 pipe line steel hot-rolling coil with a thickness of 15.9 mm. The microstructure and chemical composition of the cracks were analyzed by means of optical microscope, scanning electron microscope and energy dispersive spectroscope. The results show that the phenomenon of warping hydrops and poor effect of reverse flushing intercept descaling water in the hot rolling slab of the hot rolling process. This phenomenon leads to the local overcooling of the strip. Therefore, in the process of finishing rolling, the surface deformation of the strip nonuniform so that the pull crack was produced. The crack can be effectively controlled by improving the warping phenomenon of the rough rolling and adjusting the angle of the reverse flushing.
  • [1]
    许庆太, 魏伯,赵晓飞,等. 钢板表面纵向裂纹的金相检验和分析[J]. 理化检验(物理分册),2006,42(12):634-636.
    [2]
    杨春宝,王宝动,裴培. TRIP590热轧卷表面裂纹形成原因及保护渣优化研究[J]. 炼钢,2017,33(3):78-82.
    [3]
    师静蕊,沈冬冬,袁泽喜. SS400钢热轧板表面纵裂纹成因分析[J]. 理化检验(物理分册),2014,50(5):380-382.
    [4]
    冯翔宇,杨体绍,张苏云,等. 中厚板材表面纵裂纹成因分析[J]. 理化检验(物理分册),2004,40(11):569-572.
    [5]
    许竹桃,陈方玉,熊玉章,等. φ75 mm 45钢轧制裂纹分析[J]. 河北冶金,2008,66(4):72-74.
    [6]
    庞启航,唐荻,赵爱民,等. 热轧钢板表面翘皮缺陷的形成机理及控制[J]. 轧钢,2014,31(6):9-11.
    [7]
    张瑜,郭质江,张红斌. Q345B热轧钢板横裂缺陷产生原因分析及控制[J]. 云南冶金,2015,44(5):59-62.
    [8]
    邵峰. 金属塑性变形的不均匀性[J]. 安徽电力职工大学学报,2002,7(3):59-61.

Catalog

    Article views (4) PDF downloads (0) Cited by()

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return