Microstructure Transformation Behaviour of Austenite Cooling for SAE9310 Steel

LI Yong; WANG Chun-xu; LIU Xian-min; TIAN Zhi-ling; XU Guang-peng; ZHAO Su-wu

Materials and Mechanical Engineering > 2010 > 34(5): 12-15.

LI Yong, WANG Chun-xu, LIU Xian-min, TIAN Zhi-ling, XU Guang-peng, ZHAO Su-wu. Microstructure Transformation Behaviour of Austenite Cooling for SAE9310 Steel[J]. Materials and Mechanical Engineering, 2010, 34(5): 12-15.

Citation:

PDF (1071 KB)

Microstructure Transformation Behaviour of Austenite Cooling for SAE9310 Steel

More Information

Received Date: October 09, 2009

Graphical Abstract

Abstract

Abstract

With thermodynamic calculation software and XRD,the equilibrium transformation for SAE9310 steel after austenizing was investigated.Through expansion and metallographic methods the continuous cooling transformation curves of the steel were determined using Formastor-F II dilatometer.The results show that the equilibrium microstructure of SAE9310 steel was composed of α-Fe,γ-Fe,M23C6 and M7C3 carbides.The products of austenite transformation were granular bainite and ferrite when the cooling rate was lower than 0.056 ℃·s-1.Granular bainite could be mainly formed with small amount of martensite as the cooling rates were from 0.056 ℃·s-1 to 1.9 ℃·s-1.The products of austenite transformation were lath martensite with small quantity retained austenite when the cooling rate was higher than 1.9 ℃·s-1 and the granular bainite disappeared gradually.The hardness of the steel increased with the increase of cooling rate.
- SAE9310 steel,
- microstructure transformation,
- CCT curve,
- thermodynamic calculation

FullText(HTML)

References (7)

References

[1]	张熹,王春旭,刘宪民,等.化学成分波动对SAE9310钢淬透性和力学性能的影响[J].钢铁,2007,42(5):58-60.
[2]	李星逸,王轶农,刘文昌,等.低碳低合金贝氏体高强度钢热变形奥氏体的连续冷却转变[J].钢铁,1997,32(7):48-51.
[3]	ANDERSON J O,HELANDER T,HOGLUND L,et al.Thermo-Calc and Dictra computational tools for materials science[J].CALPHAD,2002,26(2):273-312.
[4]	AMS 6265M Steel bars,forging and tubing 1.2Cr-3.25Ni-0.12 Mo (0.07-0.13C)(SAE9310)vacuum consumable electrade remelted[S].
[5]	MANGONON P L.Effect of alloying elements on the microstructure and properties of a not-rolled low carbon low alloy bainitic stee[J].Metall Trans A,1976,9:1389-1393.
[6]	方鸿生,刘东雨,徐平光,等.贝氏体钢的强韧化途径[J].机械工程材料,2001,25(6):1-5,41.
[7]	戚正风.金属热处理原理[M].北京:机械工业出版社,1986.

Cited By

Get Citation

PDF

XML

Article views (3) PDF downloads (1)

Turn off MathJax

Article Contents

Abstract

References

Microstructure Transformation Behaviour of Austenite Cooling for SAE9310 Steel

Abstract

References

Catalog

Export File

Citation

Format

Content