    Fracture Reason Analysis of Last Stage Blade of Steam Turbine

    More Information
    • Received Date: August 15, 2007
      Graphical Abstract
      • Abstract
    • The low pressure last stage blade of certain unit fractured during operation. The fracture reason was analyzed by means of the test methods for chemical composition,mechaniced performance and metallurgical structure of blade steel. The results showed that the fatigue crack initiated. from a mechanical gap. Analysis on residual stress in X-ray showed that the residual stress was very high at crack origin area. The crack origin growed to fatigue fracture forced by alternating stress and residual stress together.
      • FullText(HTML)
      • References (2)
    • [1]
      张 栋. 某发动机级涡轮叶片排气边裂纹分析[J]. 理化检验-物理分册,2004,40(2)：87-90．
      [2]
      John Sedricks A ,著：不锈钢的腐蚀[M]. 吴 剑,译. 北京: 机械工业出版社,1986:56-65．
      • Related Articles

    Catalog

      Get Citation
      PDF
      XML
      Article views (4) PDF downloads (2) Cited by()
      Turn off MathJax
      Article Contents
      Abstract
      References

      PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING

      Address：99 Handan Road, ShanghaiPost Code: 200437

      Tel：021-65556775-361Email:pt@mat-test.com

      沪ICP备17055736号-5

      Supported by: Beijing Renhe Information Technology Co., Ltd.  Baidu Analytics

      /

      DownLoad:  Full-Size Img  PowerPoint
      Return
      Return