    JIANG Wei, DUAN An-jing. Failure Analysis for 7075 Aluminum Alloy Cylinder[J]. Materials and Mechanical Engineering, 2012, 36(6): 94-96.
    Citation: JIANG Wei, DUAN An-jing. Failure Analysis for 7075 Aluminum Alloy Cylinder[J]. Materials and Mechanical Engineering, 2012, 36(6): 94-96.

    Failure Analysis for 7075 Aluminum Alloy Cylinder

    More Information
    • Received Date: October 27, 2011
    • The 7075 aluminum alloy cylinder fractured during work, and then was analyzed through chemical composition, room temperature tensile test and fracture morphology to find the fracture reasons, and the relevant improved methods were proposed. The results show that the main reason for the aluminum alloy cylinder fracture was the mechanical property of the alloy decreasing because content of Mg was below the standard content. The micropore on oxide film extended along machining mark to cause fatigue source forning under cyclic stress, the crack extended quickly as the stress circulation intensify, and the fatigue fracture for 7075 aluminum alloy cylinder happened at last.
    • [1]
      邱惠中, 吴志红.航天用高性能金属材料的新进展[J].宇航材料工艺, 1996(2): 18-25.
      [2]
      刘宏, 赵刚, 刘春明, 等.6000系铝合金组织性能的研究进展[J].机械工程材料, 2004, 28(6): 1-5.
      [3]
      曾渝, 尹志民, 潘青林, 等.超高强铝合金的研究现状及发展趋势[J].中南工业大学学报, 2002, 33(6): 592-563.
      [4]
      吴安如, 戴晓元, 夏长青.微量银对Al-Zn-Mg-Cu系合金微观组织和力学性能的影响[J].机械工程材料, 2005, 29(12): 42-46.

    Catalog

      Article views (2) PDF downloads (2) Cited by()

      /

      DownLoad:  Full-Size Img  PowerPoint
      Return
      Return