    ZHAO Hai, ZOU Qiang, JIANG Bo, DENG Rong-jie, LU Song. Reasons Analysis on Ultrasonic Testing Poor Penetration of Rings[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2015, 51(4): 274-277.
    Citation: ZHAO Hai, ZOU Qiang, JIANG Bo, DENG Rong-jie, LU Song. Reasons Analysis on Ultrasonic Testing Poor Penetration of Rings[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2015, 51(4): 274-277.
    shu

    Reasons Analysis on Ultrasonic Testing Poor Penetration of Rings

    More Information
    • Received Date: February 07, 2014
      Graphical Abstract
      • Abstract
    • Poor penetration phenomena such as severe grass echo and heavy bottom wave loss were found when ultrasonic testing to a batch of rings with the unqualified ratio of 14%.The length of poor penetration area along circumferential direction was about 1/6 of the ring circumference.At the same time,the hardness of the rings was also lower than the specific value.Means such as chemical compositions analysis,metallographic examination were used to analyze the reasons for the poor penetration phenomenon.The results show that ultrasonic testing poor penetration of the rings was caused by the fact that the coarse crystal grain of rolling state was not completely eliminated because of the lower heat treated temperature.
      • FullText(HTML)
      • References (6)
    • [1]
      GB/T4336-2002碳素钢和中低合金钢火花源原子发射光谱分析方法(常规法)[S].
      [2]
      GB/T13298-1991钢的显微组织评定方法[S].
      [3]
      GB/T6394-2002金属平均晶粒度测定方法[S].
      [4]
      崔忠圻.金属学及热处理[M].北京:机械工业出版社,2004.
      [5]
      GB/T231.1-2009金属材料 布氏硬度试验 第1部分:试验方法[S].
      [6]
      康大韬,郭成熊.工程用钢的组织转变与性能图册[M].北京:机械工业出版社,1992:35.
      • Related Articles

    • Related Articles

      [1]DAI Keshun, YU Hongjiang, ZHOU Jingbo, JIAO Zonghan, LIU Ronghai, ZHENG Xin, LI Zhixiang. Reason for leakage of working cylinder of HBM-8 circuit breaker operating mechanism[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2025, 61(7): 59-63. DOI: 10.11973/lhjy-wl240156
      [2]CHENG Xiang, BAO Zheng, WANG Ruomin, MIAO Chunhui, CHEN Guohong, TANG Wenming. Residual life prediction of coarse-grained Super304H and TP347HFG steel tubes in service[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2025, 61(7): 16-22. DOI: 10.11973/lhjy-wl240124
      [3]TANG Kaiming, HUANG Wei, PU Xueyi, ZHANG Lei. A new corrosion method for grain size test specimen of GH4169 alloy[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2023, 59(10): 38-39. DOI: 10.11973/lhjy-wl202310009
      [4]ZHANG Jin, QIU Guomin, HUANG Siqi, MA Ronghua. Cause Analysis on Fracture of ZG15Cr2Mo1 Alloy Casting's Lifting Handle[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2018, 54(7): 512-514. DOI: 10.11973/lhjy-wl201807011
      [5]JIN Lin-kui, LIAO Sen-liang, HUANG Chi-wei, ZOU Wen-qi, FAN Kai-fu. Reasons Analysis on Cracking of Ductile Iron Sleeve of a Ship Anchor Machine[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2016, 52(10): 750-754. DOI: 10.11973/lhjy-wl201610017
      [6]CAI Yu, SU Zheng-qing, CAI Mei-yan, DENG Xian-bin. Failure Analysis on Fracture of 2Cr13 Steel Beam Sections Used for Hot-rolling Tubes[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2016, 52(8): 594-596. DOI: 10.11973/lhjy-wl201608019
      [7]WANG Bin. Grain Size Requirements and Testing of Structural Steel Products at Home and Abroad[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2015, 51(8): 564-569. DOI: 10.11973/lhjy-wl201508009
      [8]JIN Lin-kui, WANG Chun-liang, ZHAO Jian-guo. Reasons Analysis and Process Improvement of Coarse Microstructure of Gears after Carburizing and Quenching[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2015, 51(4): 259-262.
      [9]LU Ai-feng. Reason Analysis and Control of Abnormal Heat Treatment Structures of 45 Steel[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2012, 48(11): 766-769.
      [10]CHEN Guo-hua, CHEN Ling-jie. Failure Analysis on Fracture of Discharge Valve Guard of New Hydrogen Compressor[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2011, 47(10): 649-652.

    Catalog

      Get Citation
      PDF
      XML
      Article views (2) PDF downloads (0) Cited by()
      Turn off MathJax
      Article Contents
      Abstract
      References
      Related Articles

      PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING

      Address：99 Handan Road, ShanghaiPost Code: 200437

      Tel：021-65556775-361Email:pt@mat-test.com

      沪ICP备17055736号-5

      Supported by: Beijing Renhe Information Technology Co., Ltd.  Baidu Analytics

      /

      DownLoad:  Full-Size Img  PowerPoint
      Return
      Return