    CHEN Feng, JI Lin, GUO Yong-ping, CAO Yu-wei, ZHANG Xue-tao. Fracture Failure Analysis of Piston and Crosshead of DW-34.7/(11.5-53)X Type Compressor[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2010, 46(7): 450-455.
    Citation: CHEN Feng, JI Lin, GUO Yong-ping, CAO Yu-wei, ZHANG Xue-tao. Fracture Failure Analysis of Piston and Crosshead of DW-34.7/(11.5-53)X Type Compressor[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2010, 46(7): 450-455.

    Fracture Failure Analysis of Piston and Crosshead of DW-34.7/(11.5-53)X Type Compressor

    More Information
    • Received Date: August 09, 2009
    • The fracture failure reason of piston and crosshead of DW-34.7/(11.5-53)X type compressor was analyzed by means of chemical composition analysis, fracture analysis, mechanical properties testing and metallographic examination. The results showed that the main failure reason of compressor piston and crosshead was the unqualified microstructure.It made material mechanical properties can not satisfy the safe usage requests. At the same time, by reason of piston nut had not locking device, under alternating load, piston and piston rod had occured relative movement, resulting in the deterioration of the piston force, pistons first occurred failure accident,and high cycle fatigue cracks existed in crosshead, resulting in the next accident finally. At last, according to analytic results, the prevention measures were put forward.
    • [1]
      刘祥. 铸造合金力学及物理性能[M]. 北京: 机械工业出版社,1982.
      [2]
      郁永章,孙嗣莹,陈洪俊,等. 容积式压缩机技术手册[M].北京: 机械工业出版社,2000.
      [3]
      活塞式压缩机设计编写组. 活塞式压缩机设计[M]. 北京: 机械工业出版社,1974.
      [4]
      苏翼林. 材料力学[M]. 北京: 高等教育出版社,1986.

    Catalog

      Article views (0) PDF downloads (1) Cited by()

      /

      DownLoad:  Full-Size Img  PowerPoint
      Return
      Return