    ZHOU Ze-hua, LIU Li-qun, YI Yu, WANG Ze-hua, JIANG Shao-qun. Effect of KH-570/SiO2 Ratio on Corrosion Resistance of Al2O3-13% TiO2 Seal Coating in Acid Environment[J]. Corrosion & Protection, 2015, 36(2): 118-121.
    Citation: ZHOU Ze-hua, LIU Li-qun, YI Yu, WANG Ze-hua, JIANG Shao-qun. Effect of KH-570/SiO2 Ratio on Corrosion Resistance of Al2O3-13% TiO2 Seal Coating in Acid Environment[J]. Corrosion & Protection, 2015, 36(2): 118-121.

    Effect of KH-570/SiO2 Ratio on Corrosion Resistance of Al2O3-13% TiO2 Seal Coating in Acid Environment

    More Information
    • Received Date: August 21, 2014
    • Aimed at some disadvantages of conventional sealing agents used in acid environment,in order to broaden the application of plasma spray coatings in some aggressive environments,a sort of novel KH-570/SiO2 hybrid sealing agent was prepared by Sol-Gel method and sealed on the surface of plasma sprayed Al2O3-13% TiO2 coating.The effect of the content of KH-570 on corrosion resistance of the coating in acid environment was studied.The results revealed that the KH-570 hybrid material was a good candidate as a sealing agent for plasma sprayed coating,which could improve efficiently corrosion resistance of the sealed coating in acid environment.The corrosion resistance of the coatings increased and then decreased with increasing additions of KH-570.When the volume ratio of TEOS to KH-570 additions was 4∶5,the sealed coating had the best corrosion resistance in acid environment,its corrosion potential increased 61.6% than that of the unsealed coating,and the corrosion current was only 1/1767 of that of the unsealed one.
    • [1]
      江志强,席守谋,李华伦.等离子喷涂陶瓷涂层封孔处理的现状与展望[J].兵器材料科学与工程,1999,22(3):56-60.
      [2]
      SONG R,WANG C,JIANG Y,et al.Microstructure and properties of Al2O3/TiO2 nanostructured ceramic composite coatings prepared by plasma spraying[J].Journal of Alloys and Compound,2012,544:13-18.
      [3]
      AHMADIAN S,JORDAN E.Explanation of the effect of rapid cycling on oxidation,rumpling,microcracking and lifetime of air plasma sprayed thermal barrier coatings[J].Surface and Coatings Technology,2014,244:109-116.
      [4]
      LIU Z,YAN D,DONG Y,et al.The effect of modified epoxy sealing on the electrochemical corrosion behaviour of reactive plasma-sprayed TiN coatings[J].Corrosion Science,2013,75:220-227.
      [5]
      周林玉,刘莹,邵英平,等.热喷涂涂层封孔材料及其耐酸蚀性能[J].热喷涂技术,2009,1(2):39-42.
      [6]
      张志彬,阎殿然,高国旗.等离子喷涂氧化锆涂层封孔处理的研究现状[J].陶瓷,2009(1):30-33.
      [7]
      刘美淋,孙宏飞,于慧博,等.降低热喷涂涂层孔隙率的方法[J].腐蚀与防护,2007,28(4):171-173.
      [8]
      LISCANO S,GIL L,STAIA M.Effect of sealing treatment on the corrosion resistance of thermal-sprayed ceramic coatings[J].Surface and Coatings Technology,2004,188/189:135-139.
      [9]
      PANDEY S,MISHRA S.Sol-gel derived organic-inorganic hybird materials:Synthesis,characterization and application[J].Journal of Sol-Gel Science and Technology,2011,59:73-94.
      [10]
      林金娜,侯有军,曾幸荣.溶胶-凝胶法制备有机硅/SiO2杂化涂料的稳定性[J].高分子材料科学与工程,2007,23(2):128-131.
      [11]
      杨元政,张大同,刘正义.等离子喷涂陶瓷涂层的层状结构[J].暨南大学学报:医学版,1996,17(4):143-144.

    Catalog

      Article views (1) PDF downloads (2) Cited by()

      /

      DownLoad:  Full-Size Img  PowerPoint
      Return
      Return