    SHANG Yan-wei, ZHAO Mei-chun, CHEN Wei-feng, CHEN Lin-jun. Cracking Analysis on Welding Parts of Copper Pipe and Low Carbon Steel Pipe[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2010, 46(6): 385-387.
    Citation: SHANG Yan-wei, ZHAO Mei-chun, CHEN Wei-feng, CHEN Lin-jun. Cracking Analysis on Welding Parts of Copper Pipe and Low Carbon Steel Pipe[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2010, 46(6): 385-387.

    Cracking Analysis on Welding Parts of Copper Pipe and Low Carbon Steel Pipe

    More Information
    • Received Date: October 18, 2009
    • A large quantity of cracking appeared in welding parts of the copper pipe and low carbon steel pipe. The cracking reasons were analyzed by means of macro examinaton on the cracking position, chemical compositions analysis, fracture observition by SEM and microstructure inspection. The results show that the comprehensive effect, which was induced the oxygen content in the material was over standard and grain boundary weakness by long time welding, made that the structural stress and thermal stress existed in the joint. The grain boundary cracked when the stress exceeded the limit of the material. The improved measures were also brought forward on the basis of analysis.
    • [1]
      田泽生. 铜管钎焊热裂纹形成的原因与分析[J]. 制冷与空调,2002,4(2):71-72.
      [2]
      孙智,江利,应鹏展. 失效分析基础与应用[M]. 北京: 机械工业出版社,2005.
      [3]
      贾延琳,汪明朴,李周. 磷脱氧铜管焊接漏气失效分析[J]. 理化检测-物理分册,2006,42(2):92-94.

    Catalog

      Article views (1) PDF downloads (1) Cited by()

      /

      DownLoad:  Full-Size Img  PowerPoint
      Return
      Return