    WANG Bo, ZHANG Heng-hua. Wear Resistance of Martensite Stainless Steel 11Cr17 after Sulphonitrocarburizing[J]. Materials and Mechanical Engineering, 2011, 35(10): 12-15.
    Citation: WANG Bo, ZHANG Heng-hua. Wear Resistance of Martensite Stainless Steel 11Cr17 after Sulphonitrocarburizing[J]. Materials and Mechanical Engineering, 2011, 35(10): 12-15.
    shu

    Wear Resistance of Martensite Stainless Steel 11Cr17 after Sulphonitrocarburizing

    More Information
    • Received Date: July 10, 2011
      Graphical Abstract
      • Abstract
    • Wear resistance of sulphonitrocarburized martensite stainless steel 11Cr17 was tested on MM-200 wear tester. Wear area was measured and wear morphology was observed by microscopy with three dimensional ultra depth of field. The mechanism of increasing wear resistance of sulphonitrocarburized 11Cr17 steel was analyzed by microstructure, hardness gradient, EDS spectrum and XRD pattern. The results show that the 11Cr17 steel after sulphonitrocarburizing had more excellent wear resistance than high speed steel M2 under dry friction condition, because the former had a compound layer with high hardness and solid-lubricated FeS. The wear resistance of 11Cr17 steel after sulphonitrocarburizing and high speed steel M2 under oil lubrication conditions was not differen obviously.The anti-seizure property of sulphonitrocarburized 11Cr17 steel was also excellent, which could effectively delay the time of bad wear.
      • FullText(HTML)
      • References (12)
    • [1]
      江静华,蒋建清.室温盐液渗流[J].金属热处理,2002,27(12):33-35.
      [2]
      佟晓辉,陈蕴博,胡以正.Cr12MoV钢硫氮碳共渗层摩擦磨损特性研究[J].机械科学与技术,1993(增刊):21-23.
      [3]
      张双科,吴晓春.Cr12MoV钢等离子S-N-C共渗摩擦磨损特性研究[J].金属热处理,2003,28(4):24-28.
      [4]
      朱达文.论SURSULF处理[J].航空精密制造技术,1992(3):41-43.
      [5]
      SRINIVASAN P B. Sliding wear behavior of salt bath nitrocarburized medium carbon steel[J].Journal of Materials Engineering and Performance,2002,11:509-515.
      [6]
      WILLBUR P J. High current density,low energy, ion implantation of AISI-M2 tool steel for tribological applications[J]. Surface and Coatings Technology,1996,83:250-256.
      [7]
      FU Rui-dong. Solid solution nitriding technology of 15Cr-7.5 Mn-2.6Mo duplex stainless steel[J]. Transactions of Materials and Heat Treatment,2004,25(5):417-421.
      [8]
      戴兵,王博,张恒华.具有表面类金刚石膜高速钢的耐磨性能[J].机械工程材料,2010,34(4):51-54.
      [9]
      张红,宋玉悟.硫氮共渗后磨损粘着特性的研究[J].材料科学与工艺,1997,5(1):65-67.
      [10]
      RAMPRASAD M. Some studies on scuffing performance of surface treated AISI 4340 steels[J]. Journal of Tribology,2003,125(1):181-186.
      [11]
      袁相春,胡以正.非重载齿轮硫氮碳共渗层组织与抗胶合、承载特性[J].热加工工艺,1991(6):14-16.
      [12]
      戴中兴.45、45CrNi钢硫氮碳共渗层组织特性的研究[J].湘潭大学学报: 自然科学版,1992,15(2):102-108.
      • Related Articles

    Catalog

      Get Citation
      PDF
      XML
      Article views (4) PDF downloads (0) Cited by()
      Turn off MathJax
      Article Contents
      Abstract
      References

      Materials and Mechanical Engineering

      Address：99 Handan Road, ShanghaiPost Code: 200437

      Tel：021-65556775-368Email:mem@mat-test.com

      沪ICP备17055736号-5

      Supported by: Beijing Renhe Information Technology Co., Ltd.  Baidu Analytics

      /

      DownLoad:  Full-Size Img  PowerPoint
      Return
      Return