Influence of Grain Size on Hydrogen-induced Cracking Behavior of 35CrMo Steel

FENG Peng-fei; LI Chun-fu; GONG Dan-mei; SHEN Wen-zhu; CHEN Gong-jian; FU Ai-hong

Corrosion & Protection > 2012 > 33(1): 12-15.

FENG Peng-fei, LI Chun-fu, GONG Dan-mei, SHEN Wen-zhu, CHEN Gong-jian, FU Ai-hong. Influence of Grain Size on Hydrogen-induced Cracking Behavior of 35CrMo Steel[J]. Corrosion & Protection, 2012, 33(1): 12-15.

Citation:

PDF (1170 KB)

Influence of Grain Size on Hydrogen-induced Cracking Behavior of 35CrMo Steel

More Information

Received Date: February 23, 2011

Graphical Abstract

Abstract

Abstract

The grain size of 35CrMo steel was increased by heat treatment method. The influence of grain size on hydrogen embrittlement sensitivity was studied in the environment of dynamic electrochemical hydrogen charging by slow strain rate test (SSRT) technique and modern micro-analysis method. The results showed that the grain size of 35CrMo steel reached 10.8 μm by complete quenching at 850 ℃ for 15 min (oil cold), subcritical quenching at 780 ℃ for 25 min (oil cold) and high temperature tempering at 740 ℃ for 120 min (air cooling) in order. When the current density of dynamic hydrogen charging was 150 mA/cm2, the breaking strength, elongation and reduction in area of 35CrMo steel were 569.875 MPa, 12.90% and 38.96% respectively, indicating that increasing grain size is an effective way to improve the resistance to hydrogen induced cracking of 35CrMo steel.
- 35CrMo,
- SSRT,
- dynamic electrochemical hydrogen charging,
- hydrogen induced cracking,
- grain size

FullText(HTML)

References (16)

References

[1]	于青. 35CrMo高强度钢在海洋大气中的氢渗透行为与环境致脆机理研究[D]. 青岛:中国科学院海洋研究所,2008.
[2]	何家胜,崔好选,朱晓明,等. 螺栓(35CrMoA)在湿H2S环境中应力腐蚀试验研究[J]. 压力容器,2007(02):19-23.
[3]	Wang M Q,Akiyama E,Tsuzaki K. Effect of hydrogen on the fracture behavior of high strength steel during slow strain rate test[J]. Corrosion Science,2007(49):4081-4097.
[4]	Li G F,Wu R G,Lei T C. Effect of prior austenitic grain size on stress corrosion cracking of a high-strength steel[J]. Metallurgical and Materials Transactions A,1990,21(12):503-505.
[5]	Tsai T C,Chuang T H. Atmospheric stress corrosion cracking of a superplastic 7475 Aluminum Alloy[J]. Metallurgical and Materials Transactions A,1996,27(12):2617-2627.
[6]	Fuchigami H,Minami H,Nagumo M. Effect of grain size on the susccptibility of markensitic steel to hydrogen-related failure[J]. Philosophical Magazine Letters,2006,86(12):21-29.
[7]	何建宏,唐祥云, 陈南平. 晶粒大小对双相不锈钢的强度和氢致开裂的影响[J]. 金属学报,1990(04):A257-A261.
[8]	刘孝红,王毛球,时捷,等. 热处理对25CrNi2MoVNb钢氢脆敏感性的影响[J]. 金属热处理,2009(12):9-13.
[9]	翁庆宇. 超细晶钢-钢的组织细化理论与控制技术[M]. 北京:冶金工业出版社,2003:9-20.
[10]	尹志新,于维成,姚戈,等. 循环淬火细化对42CrMo钢组织及疲劳性能的影响[J]. 钢铁,2002(10):52-56.
[11]	吴玉萍,徐庆莘,肖昌利. 低合金钢亚温淬火强韧化研究[J]. 理化检验-物理分册,1997,33(2):11-12,46.
[12]	宋锦福. 亚温淬火对35CrMo钢抗氢脆性能的影响[J]. 福州大学学报(自然科学版),1989(03):39-44.
[13]	王冀恒,李惠,谢春生,等. 35CrMo钢亚温淬火强韧化组织与性能研究[J]. 材料热处理技术,2009(06):144-146.
[14]	褚武扬,于广华,程以环,等. 钢的氢致沿晶断裂理论[J]. 中国科学(E辑),1996(10):411-416.
[15]	潘川,褚武扬,李正邦,等. 氢和氢致马氏体导致不锈钢氢脆的定量研究[J]. 中国科学(E辑),2002,(6):343-349.
[16]	乔利杰,肖纪美,褚武扬,等. 奥氏体不锈钢应力腐蚀和氢致开裂裂尖区的氢浓度分布[J]. 中国腐蚀与防护学报,1989(9):235-239.

Cited By

Get Citation

PDF

XML

Article views (11) PDF downloads (1)

Turn off MathJax

Article Contents

Abstract

References

Influence of Grain Size on Hydrogen-induced Cracking Behavior of 35CrMo Steel

Abstract

References

Catalog

Export File

Citation

Format

Content