    Purity Control in Producing Metallic Strontium Using Vacuum Aluminothermic Reduction

    More Information
    • Received Date: April 02, 2007
    • Purity control in producing metallic strontium using vacuum aluminothermic reduction was analysed by thermodynamic calculation.The differentiae of the critical reduction temperature and vapor pressure of Sr,Ba and Ca were discussed,and the purity of metallic strontium was controled.The results showed that BaO was the most unstable one to be reduced easily,CaO was the most stable one to be reduced dificultly,and SrO was in between.The vapor pressure of Sr increased with higher temperature,resulting in easy distillation of Sr;At 1 273 K,the vapor pressure ratio of Sr to Ca was about 2.4,making Ca difficult to be distilled,while the ratio of Sr to Ba was about 28.5 making Ba easy to be distilled.High purity metallic strontium with w(Sr)≥99.5%,w(Ba)<0.20%,w(Ca)<0.05% can be produced using excellent-grade industrial pure strontium carbonate and pure aluminum Al99.80 under following optimized conditions,(1 050±20) ℃,0.01 kPa,15 h.
    • [1]
      高延林.锶的利用与开发[M].西宁:青海人民出版社,1995:60-65.
      [2]
      刘相果,彭晓东,谢卫东,等.金属锶及其合金的研究现状与应用[J].稀有金属,2004,28(4):750-755.
      [3]
      刘相果,彭晓东,刘江,等.高纯碳酸锶的制备技术研究进展[J].材料导报,2003,17(9):54-57.
      [4]
      杨宝刚,高炳亮,杨振海,等.制取铝锶合金在我国的研究进展[J].轻金属,1999(1):33-35.
      [5]
      Joshi M N,Grover A K,Balachandra J.Preparation of the metal strontium from celestite[J].Indian Journal of Technology,1973,11(2):74-77.
      [6]
      Joshi M N,Grover A K,Balachandra J.Studies on the aluminothermic reduction of pure strontium oxide[J].Indian Journal of Technology,1974,12(1):28-30.
      [7]
      Evers J,Oehlinger G,Weiss A,et al.Preparation and characterization of high purity calcium,strontium and barium[J].Journal of the Less-Common Metals,1981,81(1):15-31.
      [8]
      Joseph Langlais.Strontium extraction by aluminothermic reduction[D].Montreal:McGill University,1991.
      [9]
      张明杰,李继东,郭清富.真空铝热还原法生产金属锶——铝热还原工艺的研究[J].东北大学学报(自然科学版),2004,25(12):1176-1179.
      [10]
      曹大义.真空铝热还原法制取金属钙钡锶[J].有色金属(冶炼部分),2001,23(6):42-44.
      [11]
      陆庆桃,梁琥琪,黄良余.金属锶的应用和制取[J].上海金属(有色分册),1990,11(1):1-7.
      [12]
      谈荣生,于金,李凡,等.一种铝热法一次真空还原蒸馏生产工艺及金属锶:中国,200410041401.8[P].2004-07-16.
      [13]
      颜志明,刘雅娴,颜志仁,等.锶和钡等有色金属的真空热还原法的工业化生产工艺技术及其设备:中国,91107058.3[P].1992-12-16.
      [14]
      于金,蒋建清,方峰,等.真空铝热还原法制备金属锶反应机理的热力学分析及试验研究[J].金属学报,2005,41(8):824-828.
      [15]
      于金,吴三械,董 岩,等.真空铝热还原法制备金属锶的反应机理研究[J].东南大学学报(自然科学版),2006,36(6):951-955.
      [16]
      于金,吴三械,董 岩.真空铝热还原法制备金属锶的锶还原率研究[J].机械工程材料,2007,31(5):20-23.
      [17]
      梁英教,车荫昌.无机物热力学数据手册[M].沈阳:东北大学出版社,1993.

    Catalog

      Article views (2) PDF downloads (0) Cited by()

      /

      DownLoad:  Full-Size Img  PowerPoint
      Return
      Return