    Galvanizing Treatment of Aluminum Sacrificial Anode Surface and Its Electrochemical Performance

    More Information
    • Received Date: March 09, 2011
    • The surface of Al alloy-based sacrificial anodes were galvanized to different thicknesses, and the electrochemical performance of the anodes were analyzed by polarization testing, EIS and self-discharge method. The polarization curves showed that the corrosion potential of galvanized specimens shifted positively with the increase of zinc coating thickness. The results of EIS showed that the electrochemical activity of the samples increased. The results of self-discharge tests showed that there was little influence of Zn layer on the couple current as time changed, but the change of protection couple current tended to more smooth for anodes with certain thickness of Zn layer. The change of cathodic protection potential with time decreased fast firstly. then tended to be slow and stable at last. The thicker the Zn layer, the more negative the shift degree of cathodic potential.
    • [1]
      张国华,李妍. 导管架复合牺牲阳极系统和铝基牺牲阳极系统的对比分析[J]. 中国造船,2007,11(48):36-42.
      [2]
      Leonard L B. Composite anode tests indicate 30% reduction in weight and cost[J]. Offshore,1995,55(7): 20-29.
      [3]
      Rossi S,Bonora P L. Pasinetti R,et al. Laboratory and field characterization of a new sacrificial anode for cathodic protection of offshore structures[J]. Corrosion,1998,54(12):1018-1025.
      [4]
      陈孟丽. 海洋构筑物镁铝复合牺牲阳极的开发与应用研究[D]. 重庆:重庆大学,2009.
      [5]
      Ma J L,Wen J B. Corrosion analysis of Al-Zn-In-Mg-Ti-Mn sacrificial anode alloy[J]. Journal of Alloys and Compounds,2010,496(1/2):110-115.
      [6]
      郝小军,宋诗哲. 电偶电流评价牺牲阳极性能[J]. 中国腐蚀与防护学报,2005,25(3):176-178.
      [7]
      Shibli S M A,Jabeer B,Manu R. Development of high performance aluminium alloy sacrificial anodes reinforced with metal oxides[J]. Materials letters,2007,61(14/15):3000-3004.
      [8]
      黄伟九, 李兆峰, 刘明. 热扩散对镁合金锌铝涂层界面组织和性能的影响[J]. 材料热处理学报, 2007,28(2):106-109.
      [9]
      罗耀宗. 铝合金电镀前处理新工艺[J]. 电镀与涂饰,2003,22(3):55-56.
      [10]
      马洪芳,刘志宝,殷风玲. 铝合金电镀工艺研究[J]. 腐蚀与防护,2003,24(4):162-163.
      [11]
      赵平,杨佳星,王宏,等. 2024 铝合金浸锌工艺研究[J]. 轻合金加工技术,2009,37(5):41-43.

    Catalog

      Article views (16) PDF downloads (14) Cited by()

      /

      DownLoad:  Full-Size Img  PowerPoint
      Return
      Return