    Analysis on Ductile-brittle Transition Temperature of 34CrNiMo6 Steel Used for Wind Turbine Spindle

    More Information
    • Received Date: November 02, 2014
    • In order to obtain the ductile-brittle transition temperature of 34CrNiMo6 steel used for wind turbine spindle, V-type impact samples were taken at different radial positions, they were tested between -110 ℃ and 25 ℃,the result data was fitted by Boltzman function,then the temperature at 50% of the brittle fracture (FATT50) was obtained from the ductile-brittle transition temperature curve.The brittle and ductile fracture morphology of samples was observed by SEM, the brittle and plastic fracture behaviors of 34CrNiMo6 alloy were briefly analyzed.The results indicated that the ductile-brittle transition temperature of 34CrNiMo6 alloy was between -50 ℃ and -70 ℃, and the transition temperature of spindle surface was lower than that at its core position.Plastic fracture samples showed a typical dimple-like morphology, the fracture surface morphology gradually transited to cleavage fracture as the test temperature decreased.
    • [1]
      张波,范华,张邦强.34CiNiMo6材料低温韧性研究[J].东方电气评论,2013,27(105):38-43.
      [2]
      焦何生.34CiNiMo6风电主轴的热处理工艺[J].铸造,2013,17:44-45.
      [3]
      ASTM A370-2013aStandard Test Methods and Definitions for Mechanical Testing of Steel Products[S].
      [4]
      GB/T 229-2007金属材料夏比摆锤冲击试验方法[S].
      [5]
      王烽,廉晓洁.冲击韧脆转变曲线数学模型的选择[J].理化检验-物理分册,2009,45(10):617-620.
      [6]
      周昌玉,夏翔鸣.CrMo钢材料韧脆转变温度曲线的回归分析[J].压力容器,2003,20(6):13-18.
      [7]
      赵建平,张秀敏,沈士明.材料韧脆转变温度数据处理方法探讨[J].石油化工设备,2004,33(4):29-32.
      [8]
      张锦,张瑞雪,马丽,等.影响B50A224钢韧脆转变温度的因素[J].理化检验-物理分册,2015,51(2):105-108.
      [9]
      赵品.材料科学基础[M].哈尔滨:哈尔滨工业大学出版社,2007:120-143.
      [10]
      BORDET S R, KARSTENSEN A D, KNOWLES D M, et al.A new statistical local criterion for cleavage fracture in steel.Part II: application to an offshore structural steel [J].Engineering Fracture Mechanics, 2005,72:453-474.
    • Related Articles

      [1]XU Hejun, MEI Tan. Instrumented impact test for ductile-brittle transition temperature evaluation of mixed fracture metal materials[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2023, 59(10): 13-18,39. DOI: 10.11973/lhjy-wl202310003
      [2]WANG Yong. Effect of Impact Notch Type on Ductile-Brittle Transition Temperature of 34CrNi1Mo Steel[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2021, 57(10): 37-39. DOI: 10.11973/lhjy-wl202110008
      [3]YANG Jingang. Effect of Different Fitting Functions on Evaluation Results of Ductile Brittle Transition Temperature of Gas Turbine Disk[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2021, 57(7): 29-34. DOI: 10.11973/lhjy-wl202107007
      [4]XU Hejun. Some Key Problems in Testing of Ductile-Brittle Transition Temperature of Metallic Materials[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2017, 53(6): 422-427. DOI: 10.11973/lhjy-wl201706010
      [5]WU Kai-bin, YAO Yong. Measurement of Ductile-brittle Transition Temperature of 20 Steel Pipes up to Different Standards[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2016, 52(5): 300-302. DOI: 10.11973/lhjy-wl201605003
      [6]WU Bo, GAO Guang-yan, SUN Ming-ye, LI Xia-xi, WANG Xiu-yun. Ductile-brittle Transition Temperature Test of Helical Welding Pipes of a High Pressure Gas Station[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2015, 51(2): 116-119.
      [7]ZHANG Jin, ZHANG Rui-xue, MA Li, MA Wen-jin. Factors Affecting the Ductile-brittle Transition Temperature of B50A224 Steel[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2015, 51(2): 105-108.
      [8]ZHANG Jin, ZHANG Rui-xue, MA Wen-jin, QIU Guo-min. Effects of δ-Fe on Ductile-brittle Transition Temperature of ZG06Cr13Ni4Mo Stainless Steel[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2013, 49(3): 139-143.
      [9]ZHENG Cheng-ping, ZHANG Rui-feng. Effect of Alloy Element Composition Fluctuation in the Steel on the Ductile-brittle Transition Temperature[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2010, 46(4): 223-225.
      [10]YU Zhao-bin, ZHANG Zhuang. RESEARCH ON DUCTILE-BRITTLE TRANSITION TEMPERATURE OF 921A STEEL[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2006, 42(7): 332-334.

    Catalog

      Article views (11) PDF downloads (0) Cited by()

      /

      DownLoad:  Full-Size Img  PowerPoint
      Return
      Return