    YANG Zhong. BLISTER CAUSE ANALYSIS OF TP2 COPPER TUBE AFTER ANNEALING[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2008, 44(11): 661-663.
    Citation: YANG Zhong. BLISTER CAUSE ANALYSIS OF TP2 COPPER TUBE AFTER ANNEALING[J]. PHYSICAL TESTING AND CHEMICAL ANALYSIS PART A:PHYSICAL TESTING, 2008, 44(11): 661-663.

    BLISTER CAUSE ANALYSIS OF TP2 COPPER TUBE AFTER ANNEALING

    More Information
    • Received Date: August 06, 2007
    • Blister appeared on the surface of TP2 copper tube and the casting was studied by means of optical microscopy and SEM and EDS instrument. The results showed that Cu2O granules existed in TP2 copper cast ingot and extruding tube. During anneal processing in the reductive atmosphere, the air came from reductive reaction letted out to form bubbles on the tube surface.The measures to reduce the blister were discussed.
    • [1]
      张 劭. 关于紫铜熔铸中吸气的原因及其危害[J]. 特种铸造及有色合金,1998,5: 42-44.
      [2]
      郑子樵. 材料科学基础[M]. 长沙: 中南大学出版社,2005: 381.
    • Cited by

      Periodical cited type(7)

      1. 罗衡,严宗亮,阚超玉,杨驰骋,张自琪,陈子鹏. 输送管内表面高速激光熔覆铁基合金的组织与性能研究. 材料保护. 2025(02): 123-130 .
      2. 裴明源,王磊,赵京涛,王海强,高龙飞,刘代平,赵阳,范召森,刘志兰. 稀释率对激光熔覆层组织与硬度的影响. 模具工业. 2024(10): 69-76 .
      3. 范芳,肖贵乾,武昭妤,熊庆,门正兴. 某汽车覆盖件冷切边模具激光熔覆表面强化材料研究. 锻压技术. 2023(01): 208-215 .
      4. 陈冠秀,安立周,王硕,钱坤,谭业发. 激光熔覆技术的研究概况及其发展趋势. 机电产品开发与创新. 2022(05): 15-18+41 .
      5. 徐鑫,潘应君,柯德庆,潘颖慧,甘章华. 316不锈钢表面等离子熔敷硼化物覆层的组织与性能. 机械工程材料. 2021(04): 51-56 .
      6. 邓静伟,张宇,贺博,段喻,朱龙哲,李楠,冯文韬. 基于有限元的碗头挂板金具锻造成形仿真分析. 锻压技术. 2021(10): 31-37 .
      7. 石淑婷,陈建刚,舒林森,柳召. Fe-Cr-Ni粉末激光熔覆工艺优化及性能研究. 应用激光. 2021(05): 955-960 .

      Other cited types(8)

    Catalog

      Article views (6) PDF downloads (3) Cited by(15)

      /

      DownLoad:  Full-Size Img  PowerPoint
      Return
      Return