    Effects of Plasma Spraying Parameters on Wear Properties of Cr2O3 Coatings

    More Information
    • Received Date: October 20, 2007
    • Orthogonal test were conducted to explore the influence of plasma spraying parameters on wear behaviours of Cr2O3 coatings.The wear track were examined by scanning electron microsopy (SEM) and energy dispersive spectroscopy (EDS).The results show that the order of parameters affecting the wear property from major to minor is spray distance L,hydrogen flow GH2,plasma current I1 and argon gas flow GAr.The optimized parameters are plasma current 650 A,Ar gas flow 40 L·min-1,H2 gas flow 10 L·min-1 and spray distance 100 mm.It was found that wear mechanism of Cr2O3 coatings was governed by micro brittle fracture and adhesion wear.
    • [1]
      Hélène Ageorges,Pavel Ctibor,Zouhair Medarhri,et al.Influence of the metallic matrix ratio on the wear resistance (dry and slurry abrasion) of plasma sprayed cermet (chromia/stainless steel) coatings[J].Surface and Coatings Technology,2006,201:2006-2011.
      [2]
      Giovanni Bolelli,Valeria Cannillo,Luca Lusvarghi,et al.Wear behaviour of thermally sprayed ceramic oxide coatings[J].Wear,2006,261:1298-1315.
      [3]
      孙永兴,王引真,何艳玲.Cr2O3梯度涂层的组织与耐磨性研究[J].材料导报,2000,14(7):64-65.
      [4]
      李剑锋,黄静琪,季珩,等.等离子喷涂Cr2O3涂层显微硬度的工艺优化[J].硅酸盐学报,2001,29(1):49-53.
      [5]
      Celik E,Tekmen C,Ozdemir I,et al.Effects on performance of Cr2O3 layers produced on Mo/cast-iron materials[J].Surface and Coatings Technology,2003,174:1074-1081.
      [6]
      Mann B S,Prakash Braham.High temperature friction and wear characteristics of various coating materials for steam valve spindle application[J].Wear,2000,240:223-230.
      [7]
      Toma D,Brandl W,Marginean G.Wear and corrosion behaviou of thermally sprayed cermet coatings[J].Surface and Coatings Technology,2001,138:149-158.
      [8]
      Fernández J E,Wang Yinglong,Tucho R,et al.Friction and wear behaviour of plasma-sprayed Cr2O3 coatings against steel in a wide range of sliding velocities and normal loads[J].Tribology International,1996,29(4):333-343.
      [9]
      王引真,孙永兴,何艳玲.Cr2O3涂层性能与等离子喷涂工艺稳定性的关系[J].材料保护,2000,33(7):41-43.
      [10]
      Ahn Hyo-Sok,Kwon Oh-Kwan.Tribological behaviour of plasma-sprayed chrominu oxide coating[J].Wear,1999,225:814-824.
      [11]
      孙永兴,王引真,何艳玲.等离子喷涂工艺稳定性对Cr2O3涂层结合强度的影响[J].兵器材料科学与工程,2001,24(3):38-40.
      [12]
      税毅,张鹏程,白彬,等.1Cr17Ni4不锈钢金属和陶瓷等离子体喷涂工艺研究[J].表面技术,2005,34(5):53-55.

    Catalog

      Article views (3) PDF downloads (0) Cited by()

      /

      DownLoad:  Full-Size Img  PowerPoint
      Return
      Return