Surface and Cross-Section Morphology of Hot Rolling Strip Steel after Reduction and Cold Rolling

JING Yu-an; HU Xi-da; ZANG Xiao-ming; QIN Yi; LI Chun-fu

Materials and Mechanical Engineering > 2014 > 38(12): 60-64.

JING Yu-an, HU Xi-da, ZANG Xiao-ming, QIN Yi, LI Chun-fu. Surface and Cross-Section Morphology of Hot Rolling Strip Steel after Reduction and Cold Rolling[J]. Materials and Mechanical Engineering, 2014, 38(12): 60-64.

Citation:

PDF (2178 KB)

Surface and Cross-Section Morphology of Hot Rolling Strip Steel after Reduction and Cold Rolling

More Information

Received Date: September 30, 2014

Graphical Abstract

Abstract

Abstract

Hot rolling strip steel Q215 steel after being treated by reduction was rolled by cold rolling of five passes using a four-high rolling mill. The morphology of surface and cross-section of samples after reduction and different passes of cold rolling was observed using scanning electron microscopy. The results show that the defects such as cracks, bubbles and pores on the surface of test steel after reduction were eliminated in the following cold rolling. The cracks gradually decreased in width and were nearly close, but there were some traces of cracks on the surface of test steel after five passes of cold rolling and the space between cracks increased. The thickness of decarburized layer decreased with the increase of rolling pass. Surface morphology improved and surface quality enhanced constantly.
- reduction,
- cold rolling,
- iron oxide scale,
- surface morphology,
- decarburized layer

FullText(HTML)

References (10)

References

[1]	陶映初.钢铁材料的酸洗化学［M］.北京: 冶金工业出版社,1995.
[2]	董汉君,王银军.影响热轧带钢氧化铁皮酸洗质量和速度的因素［J］.机械工程材料,2009,33(3):83-89.
[3]	SAMWAYS N L. Strong competitor with traditional pickling process-hydrogen reduction scale removal process［J］.World Iron& Steel,2002(2):47-51.
[4]	PRIMAVERA A, CATTARINO S, PAVLICEVIC M.Influence of process parameters on scale reduction with H2［J］.Ironmaking and Steelmaking, 2007, 34(4):290-296.
[5]	石杰,王德仁,何业东,等.用CO还原BRC3热轧带钢表面氧化铁皮的研究［J］.钢铁,2008(5):89-93.
[6]	SHI Jie, WANG De-ren, HE Ye-dong, et al. Reduction of oxide scale on hot-rolled strip steels by carbon monoxide［J］.Materials Letters,2008,62(20):3500-3502.
[7]	于云蛟,李胜利,井玉安,等.氢气还原对热轧带钢表面形貌的影响［J］.轧钢,2012,29(5):18-21.
[8]	井玉安,于云蛟,李胜利.氮氢混合气氛下带钢表面氧化铁皮的还原［J］.热加工工艺,2013,42(18):45-48.
[9]	马正伟,刘炳.冷轧钢板表面缺陷的形成原因［J］.机械工程材料,2009,33(11):90-92.
[10]	董双鹏,宋进英,陈业熊,等.冷轧钢板表面缺陷的种类及形成原因［J］.机械工程材料,2012,36(7):100-104.

Cited By

Get Citation

PDF

XML

Article views (3) PDF downloads (0)

Turn off MathJax

Article Contents

Abstract

References

Surface and Cross-Section Morphology of Hot Rolling Strip Steel after Reduction and Cold Rolling

Abstract

References

Catalog

Export File

Citation

Format

Content