起重机钢丝绳断裂失效分析

基金项目:

上海市科委自然科学基金资助项目(12ZR1409700)

详细信息

Failure Analysis of Crane Wire Rope Fracture

摘要: 通过宏观检验、化学成分分析、力学性能检测、断口分析、金相检验等方法对某起重机钢丝绳断裂的原因进行了分析。结果表明: 钢丝绳为韧性断裂, 在使用过程中钢丝绳承受剧烈的挤压和摩擦, 导致钢丝损伤, 同时产生高温引起相变硬化, 部分受损钢丝横截面积减小, 承载能力降低, 继而发生断裂, 最终导致钢丝绳整体过载断裂。
- 钢丝绳 /
- 断裂 /
- 失效分析 /
- 摩擦磨损
Abstract: The fracture failure of the crane wire rope was analyzed by the methods of macroscopic examination, chemical composition analysis, mechanical property test, fracture analysis, metallographic examination and so on. The results show that the fracture of the wire rope was ductile. The wire rope sustained a serious extrusion and friction during use, leading to the wire damage and transformation hardening by the produced high temperature. The damage and transformation hardening caused the decrease of cross sectional area and reduced the bearing power of the wire, resulting in the wire broken and the wire rope overload fracture.
- steel wire rope /
- fracture /
- failure analysis /
- friction and wear

[1]	张德英,单联敏.钢丝绳使用中断丝原因分析［J］.金属制品, 1999, 25(3): 7-9.
[2]	肖永清.起重钢丝绳的失效分析与安全使用［J］.金属制品, 2010, 36(6): 63-67.
[3]	王新华,江爱华,高海生,等.通用桥式起重机钢丝绳断裂失效分析［J］.理化检验-物理分册, 2012, 48(4): 269-273.
[4]	汪浩.提升钢丝绳的损坏原因及防护措施［J］.煤矿机械, 2008, 29(1): 141-144.
[5]	王强. 起重机用钢丝绳的损伤形式及防治措施［J］. 港口装卸, 2007(1): 13-17.