氯离子浓度和温度对Cr3钢CO<sub>2</sub>/H<sub>2</sub>S腐蚀的影响

氯离子浓度和温度对Cr3钢CO₂/H₂S腐蚀的影响

详细信息

摘要: 研究了25 ℃下不同Cl-浓度和5 g/L Cl-浓度下不同温度对Cr3钢CO2/H2S腐蚀的影响.通过极化试验、失重试验、扫描电镜(SEM)、能谱分析(EDS)和X射线衍射(XRD)等方法分析了腐蚀速率和腐蚀产物的形貌、成分和结构.结果表明,在25 ℃时,Cr3钢的腐蚀速率随着Cl-浓度的增加大体呈降低的趋势:而随着温度的升高,Cr3钢的腐蚀速率逐渐增加:低温时的腐蚀产物主要是FeS,高温时主要是FeS1-x.
- 腐蚀 /
- Cr3钢 /
- CO2/H2S /
- Cl-浓度 /
- 温度
Abstract: The effects of Cl- concentration and temperature on corrosion of Cr3 steel in CO2/H2S environment were studied by the methods of polarization curves,weight loss experiments,SEM,EDS and XRD tests.The results showed that the corrosion rate of Cr3 steel decreased with increasing of Cl- concentration at 25 ℃ and temperature.The main products were FeS at low temperature but FeS1-x at high temperature.
- corrosion /
- Cr3 steel /
- CO2/H2S /
- Cl- concentrations /
- temperature

[1]	李鹤林,白真权,李鹏亮,等.模拟CO2/H2S环境中API N80钢的腐蚀影响因素研究[C]//第二届石油石化工业用材研究会论文集.成都:中国腐蚀与防护学会,中国石油学会,中国金属学会,2001,101-104.
[2]	任呈强.N80油管钢在含CO2/H2S高温高压两相介质中的电化学行为及缓蚀机理研究[D].西安:西北工业大学硕士学位论文,2003.
[3]	孙冬柏,李静,俞宏英,等.Ca2+和Mg2+对CO2环境中点蚀形貌的影响[J].钢铁研究学报,2001,13(3):53-56.
[4]	张清.CO2/H2S共存条件下的油管钢腐蚀规律研究[D].洛阳:河南科技大学,2004.
[5]	高泽平,周维汉.C90耐腐蚀油管用钢Cr3的开发[J].特殊钢,2006,27(2):43-45.
[6]	张忠铧,黄子阳,孙元宁,等.3Cr抗CO2和H2S腐蚀系列油套管开发[J].宝钢技术,2006,3:5-8.
[7]	焦卫东,张清,张耀宗.CO2/H2S对油气管材的腐蚀规律[J].全面腐蚀控制,2003,17(6):13-15.
[8]	严密林,赵国仙,路民旭.5种套管在含CO2、H2S模拟腐蚀环境中的耐蚀性比较[J].材料保护,1999,32(8):27-29.
[9]	李瑛,林海潮,曹楚南,等.元素硫对特高含H2S气井用油管钢的腐蚀[J].腐蚀科学与防护技术,1996,3(8):252-255.
[10]	张清.CO2/H2S共存条件下的油管钢腐蚀规律及研究进展[J].腐蚀与防护,2003,24(7):277-281.