    316L不锈钢在有机胺脱硫溶液中的耐蚀性

    张小龙, 黎建明, 邱正秋, 王建山

    张小龙, 黎建明, 邱正秋, 王建山. 316L不锈钢在有机胺脱硫溶液中的耐蚀性[J]. 腐蚀与防护, 2014, 35(5): 492-494.
    引用本文: 张小龙, 黎建明, 邱正秋, 王建山. 316L不锈钢在有机胺脱硫溶液中的耐蚀性[J]. 腐蚀与防护, 2014, 35(5): 492-494.
    ZHANG Xiao-long, LI Jian-ming, QIU Zheng-qiu, WANG Jian-shan. Anti-corrosion Performance of 316L Stainless Steel in Organic Amine Desulfurization Solution[J]. Corrosion & Protection, 2014, 35(5): 492-494.
    Citation: ZHANG Xiao-long, LI Jian-ming, QIU Zheng-qiu, WANG Jian-shan. Anti-corrosion Performance of 316L Stainless Steel in Organic Amine Desulfurization Solution[J]. Corrosion & Protection, 2014, 35(5): 492-494.

    316L不锈钢在有机胺脱硫溶液中的耐蚀性

    详细信息
      作者简介:

      张小龙(1984-),工程师,硕士,从事烟气脱硫治理及设备腐蚀与防护工作,

    • 中图分类号: TG174

    Anti-corrosion Performance of 316L Stainless Steel in Organic Amine Desulfurization Solution

    • 摘要: 采用浸泡方法研究了316L不锈钢在烧结烟气有机胺脱硫溶液中的腐蚀行为,主要对pH、温度、Cl-浓度和SO42-浓度变化引起的影响进行了分析。结果表明,316L不锈钢在脱硫溶液中存在点蚀行为,随着溶液pH、温度、SO42-浓度(60~140 g/L)、Cl-浓度(1~10 g/L)因素的变化,均有不同程度的腐蚀; 但当pH<4、温度>80 ℃、ρ(Cl-)>10 g/L时,对316L的腐蚀影响较为明显。
      Abstract: The effect of the pH, temperature, Cl- concentration and SO42- concentration on the corrosion behavior of 316L stainless steel in the sintering flue gas organic amine desulfurization solution were studied using immersion method. The results showed that 316L stainless steel had pitting corrosion behavior in the desulfurization solution, and as the solution pH, temperature, SO42- concentration (60~140 g/L), and Cl- concentration (1~10 g/L) factors changing, different degrees corrosion occured; when pH<4, temperature>80 ℃, ρ(Cl-)>10 g/L, the effect of corrosion on 316L was more obvious.
    • [1] 时瑞生. 湿法烟气脱硫系统的腐蚀原因及防腐材料的选择[J]. 环保与综合利用,2008(3): 61-64.
      [2] 李宝顺,赵丽丽,周驰,等. 湿法烟气脱硫装置的腐蚀与防护[J]. 化工机械,2009,36(6):640-643.
      [3] 郎丰军,阮伟慧,李谋成,等. 温度对316L不锈钢耐海水腐蚀性能的影响[J]. 腐蚀科学与防护技术,2012,24(1):61-64.
      [4] 李光强,张丽琴,秦庆伟,等. 氮含量和环境温度对316L不锈钢耐腐蚀性的影响[J]. 武汉科技大学学报,2009,32(3):225-228.
      [5] 葛红花,周国定,解群. 304、316L不锈钢耐氯离子和硫离子性能比较[J]. 华东电力,2005,33(9):13-15.
      [6] 李谋成,曾潮流,林海潮,等. F-对酸性介质中316不锈钢钝化性能的影响[J]. 金属学报,2001,37(10):1083-1086.
      [7] 刘佐嘉. 316L与2205不锈钢的腐蚀行为研究现状[J]. 腐蚀与防护,2010,31(2):149-153.
    计量
    • 文章访问数:  3
    • HTML全文浏览量:  0
    • PDF下载量:  3
    • 被引次数: 0
    出版历程
    • 收稿日期:  2013-07-29
    • 刊出日期:  2014-05-14

    目录

      /

      返回文章
      返回