Hydrogen Permeation and Hydrogen Induced Cracking of Drill Pipe Steel S135
-
摘要: 通过电化学渗氢技术与恒载荷拉伸试验方法,研究了不同充氢电流密度下S135钻杆用钢的氢扩散系数、试样中的可扩散氢浓度及其氢致开裂门槛应力.结果表明,S135钻杆用钢在0.5 mol/L H2SO4+0.25 g/L As2O3溶液中电化学充氢后的可扩散氢浓度C0与充氢电流密度的平方根 i 成正比,恒载荷条件下,氢致开裂门槛应力σHIC随可扩散氢浓度的对数lnC0的升高而下降.Abstract: Hydrogen permeation coefficient and diffusible hydrogen content in drill pipe steel S135 during cathodic charging with hydrogen were studied by an electrochemical method,and the hydrogen induced cracking (HIC) threshold stress of the steel was investigated using constant load tests.Experimental results showed that during dynamical charging of drill pipe steel S135 with hydrogen in 0.5 mol/ L H2SO4+0.25 g/L As2O3 solution,the concentration of diffusible hydrogen C0 was directly proportional to cathodic current density i.The threshold stress σHIC decreased linearly with increasing logarithm of hydrogen concentration lnC0 in constant load tests.
-
-
[1] 褚武扬,乔利杰,陈奇志,等.断裂与环境断裂[M].北京:科学出版社,2000:82-100. [2] 李鹤林.G105钻杆断裂分析[J].理化检验-物理分册.1983,19(3):45-50. [3] 解仲英,冯耀荣.钻杆螺纹接头纵裂与穿刺失效分析[J].石油机械,1996,24(3):14-17. [4] 冯耀荣,李鹤林.石油钻具的氢致应力腐蚀及预防[J].腐蚀科学与防护技术,2000,12(1):57-59. [5] 褚武扬,吕荣邦,乔利杰,等.油井管钢氢致开裂门槛值研究[J].金属学报,1998,34(10):1077-1083. [6] Li H L,Gao K W,Qiao L J,et al.Strength effect in SCC of high strength steel in aqueous solution corrosion[J].Corrosion,2001,57(2):295-299. [7] Lv H,Li M D,Zhang T C,et al.Hydrigen-enhanced dislocation emission,motion and nucleation of hydrogen-induced creaking for steel[J].Science in China,1997,40E:530-533. [8] Su Y J,Wang Y B,Chu W Y.Chemisorption-facilitated dislocation emission and motion,and induced nucleation of brittle nanocrack[J].Science in China,1997,40E:661-665.
计量
- 文章访问数: 3
- HTML全文浏览量: 0
- PDF下载量: 1